Abstract:The article aimed to obtain a structural material with increased plasticity and density of 98.5–99.5% based on (Mo–25% W)–20 vol.% Cu pseudoalloys with a homogeneous refractory skeleton obtained by a single-time pressing and sintering of the dispersed mixture at temperatures 1400–1500°C. The production of a dispersed granulated Mo–25% W alloy with a powder particle size of 0.1–0.3 μm through the decomposition of complex ammonium paramolybdate and paratungstate salts into oxide compounds xWO3 · yMoO3 with their subsequent reduction by hydrogen in a rotary chamber was studied. Considering the temperature and decomposition time of complex salts in the moving layers, the physical and technological properties (such as phase composition, oxygen content, specific surface, bulk density, and tap density) of complex oxide powders xWO3 · yMoO3 and metal Mo– 25% W powders after reduction by hydrogen were compared with the corresponding properties of powders obtained in a stationary tube furnace in fixed layers. Temperature dependencies of porosity in (Mo–25% W)–20 vol.% Cu pseudoalloys after sintering at the temperature between 900 and 1500°C has been examined. It has been established that compaction of dispersed powder mixtures of (Mo–25% W)–20 vol.% Cu and homogenization of Mo–25% W alloy after sintering begin at the temperature 300°C lower than when sintering mechanical mixtures of commercial metal powders. It has been shown that (Mo–25% W)–20 vol.% Cu pseudoalloys obtained by liquid-phase sintering at 1500°C for 1 hour have the following characteristics: at 20°C, the ultimate tensile strength σt == 490 MPa, relative elongation δ = 1.1, Brinell hardness HB = 3.3 GPa, and at 500°C— σt == 370 MPa, δ = 4.4, and HB = 2.7 GPa.

Phase Evolution of Mo-W-Cu Alloy Rapid Prepared by Spark Plasma Sintering

Phase, Microstructure and Properties Evolution of Fine-Grained W–Mo–Ni–Fe Alloy During Spark Plasma Sintering

Pressure Effects on a Novel W-Mo-Cu Alloy by Large Current Electric Field Sintering: Sintering Behavior, Microstructure and Properties

Densification and Properties Investigation of W-Mo-Cu Composites Prepared by Large Current Electric Field Sintering with Different Technologic Parameter

Preparation and properties of W-Mo-Cu composite using solution combustion synthesized W Mo solid solution nanopowder

Process Parameter Optimization and Improved Properties of Large Electric Current-Sintered Mo-W-Cu Alloys Using Orthogonal Analysis

Morphological Characteristics of W/Cu Composite Nanoparticles with Complex Phase Structure Synthesized via Reactive Radio Frequency (RF) Thermal Plasma

Ablation resistance and current-carrying friction performance of WMoCu alloy with different Mo contents

Regulated Phase Separation in Al–Ti–Cu–Co Alloys through Spark Plasma Sintering Process

Enhancing the physical properties of Mo-Cu composites through plasma spheroidized spherical molybdenum powder

Impact of Cu Content on Microstructural Evolution and Mechanical Behavior of CoCrMo0.5TiVCux High-Entropy Alloys

Multiphase strengthening mechanism of Cu-Y2O3/W composites prepared by mechanical alloying

Investigation of W phase crystal structure and evolution mechanism based on Al-Cu-Sc alloy during homogenization

Enhanced Mechanical and Electrical Properties of CuCrZr-WC Alloy Prepared by Mechanical Alloying and Spark Plasma Sintering

High-Density Mo–W–Cu Pseudoalloys Based on Homogenous Mo–25% W Powder Alloy Produced by Reducing Oxide Powders in Moving Layers

In Suit Synthesis and Bonding of Cu to W–Cu Composite by Combustion Synthesis and Centrifugal Infiltration

Synthesis, Characterization, and Dealloying of Al-Cu Alloys Prepared Using Spark Plasma Sintering

Heterogeneous Morphologies and Hardness of Co-Sputtered Thin Films of Concentrated Cu-Mo-W Alloys

Superconductivity And High Hardness In Metal-Rich Carbides More2c And Wre2c

Preparation of fine-grained MoW solid solution alloys with excellent performances

Preparation and properties of Al2O3 dispersed fine-grained W-Cu alloy