Abstract:Low vacuum and high temperature typically promote the evaporation of moisture and exacerbate concrete shrinkage cracking, which highlights the issue of volume stability for concrete materials in some engineering environments (e.g. the operational environment of ultra-high-speed train in the low-vacuum tube). To evaluate its impact on moisture transport and drying shrinkage of mature concrete, different air pressure and temperature conditions were selected and the correspondent experiments of investigating moisture loss, internal relative humidity, and drying shrinkage after exposure were conducted. And the evolution of different types of moisture, hydration degree, pore structure, and morphology of matrix was analyzed through microscopic testing methods. Experimental results present that compared to the standard drying condition, the moisture loss and drying shrinkage of concrete under low vacuum and high temperature condition increased by more than 48.5 % and 77.4 % respectively. There exists a strong correlation between moisture loss and drying shrinkage of matrix after low vacuum and high temperature exposure. Besides, compared to the sole effect of low vacuum, the coupling effect of low vacuum and high temperature has a more significant impact on the moisture transport and drying shrinkage of concrete. Among them, after prolonged exposure to low vacuum and high temperature, the internal relative humidity of matrix drops to 50 %similar to 60 %, and the corresponding critical aperture reduces to 1.0-1.5 nm, thereby significantly increasing the shrinkage stress of concrete. Furthermore, low vacuum and high temperature condition reduces the content of capillary water, gel water, and chemically combined water, and leads to the loss of moisture in smaller pores. In addition, for mature concrete, low vacuum and high temperature condition not only impedes cement hydration but also induces the coarsening of pore structure, resulting in an increase in the number of macropores and pores around 50 nm, which correlates highly with the evolution of drying shrinkage.

Study on the Process of Isothermal Continuous Drying and Its Effect on the Strength of Concrete of Different Strength Grades

Experimental Research on Drying Control Condition with Minimal Effect on Concrete Strength

Isothermal Drying Process and Its Effect on Compressive Strength of Concrete in Multiscale

Preliminary experimental investigation of drying process of concrete under different temperature

Effect of Moisture Content and Porosity on Compressive Strength of Concrete During Drying at 105 °C

Effect of Elevated Temperatures on Compressive Strength of Concrete

Effect of Different Humidity-Controlling Modes on Microstructure and Compressive Behavior of Ordinary Concrete

Experimental research on strength decaying of concrete with different grades at elevated temperature

Predicting the Drying of Concrete by an Anomalous Diffusion Model

Numerical Analysis of Drying Shrinkage in Long Reinforced Concrete Structure

Effect of Moisture Content on Compressive and Split Tensile Strength of Concrete

Experimental Investigation on Strength and Deformation of Self-compacting Concrete at Elevated Temperature

Influence of Low Vacuum and High Temperature Condition on Moisture Transport and Dry Shrinkage of Mature Concrete

Effects of the Cooling Treatment on the Dynamic Behavior of Ordinary Concrete Exposed to High Temperatures

Effects of Temperature on Drying Shrinkage of Concrete

Experimental Study on the Internal Relative Humidity in Concrete under Dry-Wet Cycles

Effect of Thermal Parameters on Hydration Heat Temperature and Thermal Stress of Mass Concrete

Effect of Temperature on Pore Structure and Strength of Concrete

Experimental Study on Static Mechanical Properties and Moisture Contents of Concrete under Water Environment

Effect of thermal fatigue on mechanical properties and microstructure of concrete in constant ambient humidity

Microstructural modeling of moisture-thermal and mechanical behavior within concrete during drying at elevated temperatures