Abstract:High -strength concrete (HSC) suffers severe shrinkage, which deteriorates the structural safety of buildings over time. Therefore, this study aims to search for indexes that could reflect the development of early drying shrinkage in HSC with different types/quantities of minerals. The influences of minerals on the internal pore structure and water evaporation of HSC were investigated by experimental work, whose correlation with early drying shrinkage was clarified. The results indicated that pore size distribution (PSD) and water evaporation of HSC should be taken into account simultaneously, facilitating the proposal of a two -factor parameter, rs, and a smaller rs was accompanied by greater drying shrinkage of samples. In addition, only partial mesopore lost water that led to drying shrinkage of HSC instead of water in all mesopores. Finally, an early drying shrinkage model of HSC based on rs was established correspondingly, which was in line with the experimental data, showing great accuracy, suitability and values in practice in reflecting early drying shrinkage behaviors of the HSC selected in this study. However, the current model is based on pore structure parameters obtained from mercury intrusion porosimetry (MIP). The backscattered electron image analysis (BSE-IA) measurement of pore structure indicates that MIP underestimates the content of pores larger than 200 nm. Therefore, the actual parameter rs should be greater than the currently calculated value. In the future, with the development of pore structure testing techniques, a more accurate rs value that closely represents the true value should be obtained, and a more universal model that considers several factors should be established.

Numerical Analysis of Drying Shrinkage in Long Reinforced Concrete Structure

Concrete Thermal Cracking Analysis with Cement Hydration Model and Equivalent Age Method

Influence of Steel Reinforcement on Shrinkge Stress of Concrete

Identification of Indexes That Could Reflect Early Drying Shrinkage of High Strength Concrete with Minerals

Finite element analysis of temperature effect and crack-control measures for ultra-long concrete structures

Numerical Study of Shrinkage Cracking in Concrete and Concrete Repair Systems

Theoretical Modeling and Verification of Concrete Moisture Diffusion Surface Factor

Analytical Prediction and Experimental Research on Shrinkage Cracking of Restrained Early-Age Concrete

Influence of Flexural Loading on Chloride Ingress in Concrete Subjected to Cyclic Drying-Wetting Condition

Shrinkage Stress in Concrete under Dry–wet Cycles: an Example with Concrete Column

Calculation of Shrinkage Stress in Concrete Structures with Impact of Internal Curing

Numerical Analysis of Softening Relationship for Early-Age Concrete

Early Age Properties and Cracking Control of Concrete

Evaluation of shrinkage induced cracking in early age concrete: From ring test to circular column

Simulation and analysis of infilled-wall cracks' development by shrinkage using semi-discrete and whole type model

Investigation of drying-induced non-uniform deformation, stress, and micro-crack propagation in concrete

Numerical Simulation of Fracture and Damage Behaviour of Concrete at Different Ages

Drying shrinkage crack simulation and meso-scale model of concrete repair systems

Mechanical properties and numerical simulation of crack interface in reinforced concrete

Numerical simulation of the freezing process of concrete

Stresses Due To Autogenous Shrinkage And Drying Shrinkage In Hsc And Its Evaluation