Crystal Structure, Phase Composition and Microwave Dielectric Properties of Ca3MSi2O9 Ceramics

Xiao-Qiang Song,Kang Du,Xian-Zhe Zhang,Jie Li,Wen-Zhong Lu,Xiao-Chuan Wang,Wen Lei

DOI: https://doi.org/10.1016/j.jallcom.2018.04.044

IF: 6.2

2018-01-01

Journal of Alloys and Compounds

Abstract:Ca3MSi2O9 (M = Zr, Hf, Sn1-xTix; x = 0-0.40) low-permittivity microwave dielectric ceramics with cuspidine structure were prepared using conventional solid-state method at 1325 degrees C-1400 degrees C for 10 h in air. The lattice parameters of Ca3MSi2O9 (CMS) linearly decreased when M changed from Zr to Sn0.85Ti0.15, and a single phase was formed. For M = Sn1-xTix (x= 0.20-0.40), a second phase of CaTiO3 (CT) appeared. The relative permittivity (epsilon(r)), quality factor (Q x f), and temperature coefficient of resonant frequency (tau(f)) were closely related to ionic polarizability, relative covalence of M site, unit-cell volume, and CaTiO3 second phase. As a result, the highest Q x f value of 72840 GHz was obtained for M = Sn0.95Ti0.05, and near zero tau(f) value was achieved for M = Sn0.2Ti0.30. The microwave dielectric properties of which are as follows: epsilon(r) = 11.07, Q x f = 42400 GHz, and tau(f) = -5.1 ppm/degrees C. (C) 2018 Elsevier B.V. All rights reserved.