Abstract:In consolidation of AlON, the extensive decomposition of AlON into α-Al2O3 and AlN during sintering is one of the major reasons that significantly retard its densification process. To accelerate densification of AlON, an ultra-low concentration of La2O3 (0.03 wt%) and Y2O3 (0.02-0.04 wt%) was co-doped as sintering additives to inhibit decomposition of AlON during sintering for fast fabrication of highly transparent AlON ceramics. The phase transformation, microstructure evolution and densification process of the samples undoped and doped additive during heating were studied to investigate the densification mechanism. The results reveal that, compared to the samples undoped additive and single-doped with La2O3, the α-Al2O3 content of the samples co-doped with La2O3 and Y2O3 is significantly deduced at ≤1600 °C, which indicates that the decomposition of AlON is effectively inhibited by co-doping La2O3 and Y2O3. The reduction of α-Al2O3 along with the deceleration effect of La3+ on mass transfer, contributes to more small particles being conserved at high temperatures. Base on this, at later stage of sintering, benefiting from the enhanced mobility of grain boundary by Y3+, AlON ceramics with high relative density (99.79 %) and excellent transparency were obtained via pressureless sintering at 1880 °C for 2.5 h by co-doping 0.03 wt% La2O3 and 0.04 wt% Y2O3. The maximum transmittance of the fabricated AlON ceramics is up to 81.6 % at 3600 nm, and a transmittance of 76.0 % was measured at 400 nm. The ultra-low doping amount of La2O3 and Y2O3 and the high relative density should be the main reasons that lead to the outstanding transparency of the obtained AlON. Additionally, the fabricated AlON ceramics also exhibit a high Vickers hardness of 18.89 ± 0.18 GPa.

Transparent AlN ceramics sintered from nanopowders produced by the wet chemical method

Transparent AlON ceramics by nitriding combustion synthesis precursors and pressureless sintering method

AlON transparent ceramics from powders synthesized by improved direct nitridation

Pressureless sintering of transparent AlON ceramic with assimilable γ‐Al 2 O 3 as sintering promoting additives

Effects of AlN content on mechanical and optical properties of AlON transparent ceramics

Hot isostatic pressing of transparent AlON ceramics assisted by dissolution of gas inclusions

Investigation of the structural characteristics, dielectric properties, and infrared reflectivity spectra of AlON transparent ceramics

High-performance aluminum nitride made by Vat photopolymerization through optimization of resin refractive index and plasticizer content

Fabrication of highly transparent AlON ceramics by inhibiting decomposition of AlON

Thermal Conductivity of AlN Ceramics Sintered with CaF2 and YF3

Fabrication and properties of highly transparent Li0.07Al2.76O3.64N0.36 ceramics by aqueous gelcasting and two-step preparation

A Fast Pressureless Sintering Method for Transparent AlON Ceramics by Using a Bimodal Particle Size Distribution Powder

Phase composition, microstructure, electrical and thermal properties of TiN and Yb2O3-Sm2O3 doped AlN ceramics

Thermal Conductivity of AlN Ceramics with CaF2-YF3 Addition

Balancing thermal conductivity and strength of hot-pressed AlN ceramics via pre-sintering and annealing process

Microstructure and thermal conductivity of AlN ceramics with ultra-fine Y2O3 powder addition

Preparation of transparent MgAlON ceramics with tunable compositions

Microstructure of low-temperature sintered AlN

Microstructure and thermal conductivity of aluminium nitride with (CaY)F3 as the sintering aid

Effect of nitrogen content on optical properties of transparent γ-AlON polycrystalline ceramics

Low-Temperature Sintering of AlN Ceramics by Sm 2 O 3 -Y 2 O 3 -Cao Sintering Additives Formed Via Decomposition of Nitrate Solutions