Abstract:In consolidation of AlON, the extensive decomposition of AlON into α-Al2O3 and AlN during sintering is one of the major reasons that significantly retard its densification process. To accelerate densification of AlON, an ultra-low concentration of La2O3 (0.03 wt%) and Y2O3 (0.02-0.04 wt%) was co-doped as sintering additives to inhibit decomposition of AlON during sintering for fast fabrication of highly transparent AlON ceramics. The phase transformation, microstructure evolution and densification process of the samples undoped and doped additive during heating were studied to investigate the densification mechanism. The results reveal that, compared to the samples undoped additive and single-doped with La2O3, the α-Al2O3 content of the samples co-doped with La2O3 and Y2O3 is significantly deduced at ≤1600 °C, which indicates that the decomposition of AlON is effectively inhibited by co-doping La2O3 and Y2O3. The reduction of α-Al2O3 along with the deceleration effect of La3+ on mass transfer, contributes to more small particles being conserved at high temperatures. Base on this, at later stage of sintering, benefiting from the enhanced mobility of grain boundary by Y3+, AlON ceramics with high relative density (99.79 %) and excellent transparency were obtained via pressureless sintering at 1880 °C for 2.5 h by co-doping 0.03 wt% La2O3 and 0.04 wt% Y2O3. The maximum transmittance of the fabricated AlON ceramics is up to 81.6 % at 3600 nm, and a transmittance of 76.0 % was measured at 400 nm. The ultra-low doping amount of La2O3 and Y2O3 and the high relative density should be the main reasons that lead to the outstanding transparency of the obtained AlON. Additionally, the fabricated AlON ceramics also exhibit a high Vickers hardness of 18.89 ± 0.18 GPa.

Hot isostatic pressing of transparent AlON ceramics assisted by dissolution of gas inclusions

Pressureless sintering of transparent AlON ceramic with assimilable γ‐Al 2 O 3 as sintering promoting additives

Transparent MgAl2O4 ceramics prepared by microwave sintering and hot isostatic pressing

A new and highly active sintering additive: SiO2 for highly-transparent AlON ceramic

Highly Transparent Alon Pressurelessly Sintered from Powder Synthesized by A Novel Carbothermal Nitridation Method

Preparation of transparent MgAlON ceramics with tunable compositions

Fabrication of highly transparent AlON ceramics by inhibiting decomposition of AlON

A Fast Pressureless Sintering Method for Transparent AlON Ceramics by Using a Bimodal Particle Size Distribution Powder

Highly-transparent AlON ceramic fabricated by tape-casting and pressureless sintering method

Investigation of the structural characteristics, dielectric properties, and infrared reflectivity spectra of AlON transparent ceramics

Transparent AlON ceramics by nitriding combustion synthesis precursors and pressureless sintering method

Fast pressureless sintering of highly transparent AlON ceramics by reducing Y enrichment with nano-sized granular Y 2 O 3 as additive

Fabrication of transparent MgAl<sub>2</sub>O<sub>4</sub> ceramics by gelcasting and cold isostatic pressing

Lowering hot isostatic pressing temperature of ultrafine‐grained MgAl2O4 transparent ceramics by two‐step pre‐sintering

Transparent AlN ceramics sintered from nanopowders produced by the wet chemical method

Two-step pressureless sintering of ultrafine powders for the preparation of high strength and transmittance AlON ceramics

AlON transparent ceramics from powders synthesized by improved direct nitridation

Reactive sintered highly transparent AlON ceramics with Y 2 O 3 ‐MgAl 2 O 4 ‐H 3 BO 3 ternary additive

Investigation on Mechanical Properties of AlON Ceramics Synthesized by Spark Plasma Sintering

Enhancement of the Densification and Mechanical Properties of Aluminum-Doped Zinc Oxide Ceramics by Hot Isostatic Pressing

Hot-pressing of Translucent Y-α-SiAlON Ceramics Using Ultrafine Mixed Powders Prepared by Planetary Ball Mill