Study on AlON phase evolution and densification behavior as a function of particle size and doping amount
Yingchun Shan,Ping Li,Xiannian Sun,Xiaodong He,Changqing Hong,Jiujun Xu,Jiangtao Li
DOI: https://doi.org/10.1016/j.jeurceramsoc.2020.05.019
IF: 5.7
2020-09-01
Journal of the European Ceramic Society
Abstract:<p>Three groups of AlON powders with D<sub>50</sub> = 0.5, 1.1 and 2.7 μm (referred as P0.5, P1.1 and P2.7) were prepared to study the pressureless sintering behavior of AlON. These powders were doped with 0-0.75 wt.% Y<sub>2</sub>O<sub>3</sub> to investigate the combined effect of powder size and doping amount on the phase transformation, microstructure evolution and densification process during heating. The addition of high additive amount to P0.5 and P1.1 powders resulted in massive transformation into α-Al<sub>2</sub>O<sub>3</sub> and AlN, which resulted in agglomeration of α-Al<sub>2</sub>O<sub>3</sub> and isolation of AlN. Although low amount of additive to all three powders can effectively inhibit agglomeration of α-Al<sub>2</sub>O<sub>3</sub> and homogenization of particle size before sintering, its sintering ability is insufficient. 0.05, 0.10 and 0.50 wt.% Y<sub>2</sub>O<sub>3</sub> is the optimal addition to P0.5, P1.1 and P2.7 powders, respectively, to obtain high density, i.e. the larger of AlON powder size, the more Y<sub>2</sub>O<sub>3</sub> is needed.</p>
materials science, ceramics