Abstract:In consolidation of AlON, the extensive decomposition of AlON into α-Al2O3 and AlN during sintering is one of the major reasons that significantly retard its densification process. To accelerate densification of AlON, an ultra-low concentration of La2O3 (0.03 wt%) and Y2O3 (0.02-0.04 wt%) was co-doped as sintering additives to inhibit decomposition of AlON during sintering for fast fabrication of highly transparent AlON ceramics. The phase transformation, microstructure evolution and densification process of the samples undoped and doped additive during heating were studied to investigate the densification mechanism. The results reveal that, compared to the samples undoped additive and single-doped with La2O3, the α-Al2O3 content of the samples co-doped with La2O3 and Y2O3 is significantly deduced at ≤1600 °C, which indicates that the decomposition of AlON is effectively inhibited by co-doping La2O3 and Y2O3. The reduction of α-Al2O3 along with the deceleration effect of La3+ on mass transfer, contributes to more small particles being conserved at high temperatures. Base on this, at later stage of sintering, benefiting from the enhanced mobility of grain boundary by Y3+, AlON ceramics with high relative density (99.79 %) and excellent transparency were obtained via pressureless sintering at 1880 °C for 2.5 h by co-doping 0.03 wt% La2O3 and 0.04 wt% Y2O3. The maximum transmittance of the fabricated AlON ceramics is up to 81.6 % at 3600 nm, and a transmittance of 76.0 % was measured at 400 nm. The ultra-low doping amount of La2O3 and Y2O3 and the high relative density should be the main reasons that lead to the outstanding transparency of the obtained AlON. Additionally, the fabricated AlON ceramics also exhibit a high Vickers hardness of 18.89 ± 0.18 GPa.

Effects of various rare-earth additives on the sintering and transmittance of γ-AlON

Pressureless sintering of transparent AlON ceramic with assimilable γ‐Al 2 O 3 as sintering promoting additives

Fast pressureless sintering of highly transparent AlON ceramics by reducing Y enrichment with nano-sized granular Y 2 O 3 as additive

Reactive sintered highly transparent AlON ceramics with Y 2 O 3 ‐MgAl 2 O 4 ‐H 3 BO 3 ternary additive

Fabrication of highly transparent AlON ceramics by inhibiting decomposition of AlON

Effects of AlN content on mechanical and optical properties of AlON transparent ceramics

Transparent AlON ceramics by nitriding combustion synthesis precursors and pressureless sintering method

A Fast Pressureless Sintering Method for Transparent AlON Ceramics by Using a Bimodal Particle Size Distribution Powder

Simultaneously significant transparency enhancement and efficient temperature feedback achieved in AlON ceramic through luminescent rare earth doping

Effects of Y2O3 and Yttrium Aluminates As Sintering Additives on the Thermal Conductivity of AlN Ceramic Substrates

Sintering Behavior, Microstructure and Mechanical Properties of Various Fluorine-Containing Y-SiAlON Glass-Ceramics

Two-step pressureless sintering of ultrafine powders for the preparation of high strength and transmittance AlON ceramics

The role of magnesium oxide addition in densification of AlON transparent ceramics by pressureless sintering

Effect of nitrogen content on optical properties of transparent γ-AlON polycrystalline ceramics

Influence of Gd2O3 on the microstructure and properties of transparent MgAl2O4: Cr3+ ceramic

Preparation of transparent MgAlON ceramics with tunable compositions

AlON transparent ceramics from powders synthesized by improved direct nitridation

Transparent AlN ceramics sintered from nanopowders produced by the wet chemical method

Effects of Sintering Aids on the Transparency and Conversion Efficiency of Cr4+ Ions in Cr: YAG Transparent Ceramics

Compositional tailoring effect on crystal structure, mechanical and thermal properties of γ-AlON transparent ceramics

Preparation of transparent AlON from powders synthesized by novel CRN method