Abstract:In consolidation of AlON, the extensive decomposition of AlON into α-Al2O3 and AlN during sintering is one of the major reasons that significantly retard its densification process. To accelerate densification of AlON, an ultra-low concentration of La2O3 (0.03 wt%) and Y2O3 (0.02-0.04 wt%) was co-doped as sintering additives to inhibit decomposition of AlON during sintering for fast fabrication of highly transparent AlON ceramics. The phase transformation, microstructure evolution and densification process of the samples undoped and doped additive during heating were studied to investigate the densification mechanism. The results reveal that, compared to the samples undoped additive and single-doped with La2O3, the α-Al2O3 content of the samples co-doped with La2O3 and Y2O3 is significantly deduced at ≤1600 °C, which indicates that the decomposition of AlON is effectively inhibited by co-doping La2O3 and Y2O3. The reduction of α-Al2O3 along with the deceleration effect of La3+ on mass transfer, contributes to more small particles being conserved at high temperatures. Base on this, at later stage of sintering, benefiting from the enhanced mobility of grain boundary by Y3+, AlON ceramics with high relative density (99.79 %) and excellent transparency were obtained via pressureless sintering at 1880 °C for 2.5 h by co-doping 0.03 wt% La2O3 and 0.04 wt% Y2O3. The maximum transmittance of the fabricated AlON ceramics is up to 81.6 % at 3600 nm, and a transmittance of 76.0 % was measured at 400 nm. The ultra-low doping amount of La2O3 and Y2O3 and the high relative density should be the main reasons that lead to the outstanding transparency of the obtained AlON. Additionally, the fabricated AlON ceramics also exhibit a high Vickers hardness of 18.89 ± 0.18 GPa.

Preparation of transparent AlON from powders synthesized by novel CRN method

AlON transparent ceramics from powders synthesized by improved direct nitridation

Transparent AlON ceramics by nitriding combustion synthesis precursors and pressureless sintering method

Rapid synthesis of AlON powders by nitriding combustion synthesis precursor

Two-step pressureless sintering of ultrafine powders for the preparation of high strength and transmittance AlON ceramics

Effects of AlN content on mechanical and optical properties of AlON transparent ceramics

Reactive sintered highly transparent AlON ceramics with Y 2 O 3 ‐MgAl 2 O 4 ‐H 3 BO 3 ternary additive

Fabrication of highly transparent AlON ceramics by inhibiting decomposition of AlON

Fast pressureless sintering of highly transparent AlON ceramics by reducing Y enrichment with nano-sized granular Y 2 O 3 as additive

Pressureless sintering of transparent AlON ceramic with assimilable γ‐Al 2 O 3 as sintering promoting additives

A Fast Pressureless Sintering Method for Transparent AlON Ceramics by Using a Bimodal Particle Size Distribution Powder

Gas‐Phase and Solid‐State Simultaneous Mechanism for Two‐Step Carbothermal AlON Formation

Optical properties of powder and ceramics of aluminium oxynitride obtained by self-propagating high-temperature synthesis

Effects of milling time on phase assemblages of AlON powders synthesized by CTRN

Preparation of transparent MgAlON ceramics with tunable compositions

Highly-transparent AlON ceramic fabricated by tape-casting and pressureless sintering method

Direct tape casting of Al2O3/AlN slurry for AlON transparent ceramic wafers via one-step reaction sintering

Investigation of the structural characteristics, dielectric properties, and infrared reflectivity spectra of AlON transparent ceramics

Compositional tailoring effect on crystal structure, mechanical and thermal properties of γ-AlON transparent ceramics

Preparation of NiAl2O4/Al2O3 composite nanopowder

CRN synthesis of β-SiAlON from a nanocomposite precursor of mesoporous silica–alumina (Al-SBA-15) with poly 4-vinyl pyridine