Abstract:Abstract High density polyethylene (HDPE) is widely used in city water and gas piping system and even in nuclear engineering for its excellent properties in flexibility, impact resistance, aging and corrosion resistance, reliable connection, long service life. It is generally believed that the typical failure mode of PE pipe under long-term static pressure load is the slow crack growth (SCG) caused by creep crack initiation (CCI) and creep crack growth (CCG), which is a kind of quasi-brittle failure. Scratching often occurs during PE pipe installation due to the drag of pipe without any protection, which would leave axial cracks as the initial defect. This would harm the long term performance of pressurized HDPE pipe. In the present work, the creep crack kinetics was experimentally determined in term of C* integral, and then CCG behavior of PE pipe with axial semi-elliptical crack was discussed. With the help of a CARE electronic universal testing machine and DIC displacement measuring system, creep tests are performed with smooth bar specimen of PE100 pipe parent material. And the stationary creep law parameters were determined. The crack opening displacement (COD) rates were determined by creep cracking test with cracked round bar specimen. With the help of compliance calibration tests, the COD curves were changed into crack propagation curves and the creep crack kinetics was eventually determined in term of C* integral. By assuming an semi-elliptical crack front with nearly the same C* integral, the creep crack propagation was predicted with the determined crack kinetics. And the allowable initial crack size was also determined for the PE pipe discussed. Compared with that determined in terms of SIF, current study yields much margin for the allowable initial crack.

Viscoelastic and Damage Model of Polyethylene Pipe Material for Slow Crack Growth Analysis

Mechanism of Slow Crack Growth in Polyethylene: A Finite Element Approach

Short-Term Mechanical Analysis of Polyethylene Pipe Reinforced by Winding Steel Wires Using Steel Wire Spiral Structural Finite Element Model

Study on Viscoelastic Behavior During Slow Crack Growth of Medium Density Polyethylene Pipes

Prediction of Ductile Rupture Failure Life of HDPE Pipe

Probabilistic model to predict longitudinal fracture failure of buried pvc pipes

Investigation On Creep-Rupture Failure Time Of Hdpe Pipe Under Hydrostatic Pressure

Quantitative Assessment of Damage in Buried Polyethylene Pipe Subjected to Land Subsidence

Review on New Test Methods Based on Strain Hardening and Cyclic Loading of Slow Crack Growth for Polyethylene Pipes

CCG of PE100 and Life Prediction of PE Pipe With Axial Semi-Elliptical Crack

Study On Constitutive Modeling For Large Deformation Behavior Of Polyethylene Considering Strain Rate Effect

Elastoplastic Pipe-Soil Interaction Analyses of Partially-Supported Jointed Water Mains

An Analytical Model For The Progressive Failure Prediction Of Reinforced Thermoplastic Pipes Under Axial Compression

Finite Element Analysis of Polyethylene Pipe Butt Fusion Joints with Circumferential Surface Cracks

Research on Slow Crack Growth Resistance of PE Pipes Based on Correlation between Strain Hardening and Microstructure

Multiaxial Ratcheting-Fatigue Evaluation of Pressurized Elbow Pipe under Strong Cyclic Loading Using Damage-Coupled Cyclic Plasticity Model

Nonlinear Time-Dependent Mechanical Behavior of Medium-Density Polyethylene Pipe Material

Finite Element Analysis of Buried Polyethylene Pipe Subjected to Seismic Landslide

Brittle Failure in PE Pipes with Flaw Based on Nonlinear Viscoelastic Theory

A Comprehensive Review of Polyethylene Pipes: Failure Mechanisms, Performance Models, Inspection Methods, and Repair Solutions

Strain Rate-Dependent Hyperbolic Constitutive Model for Tensile Behavior of PE100 Pipe Material