Abstract:Creep rupture assessment is a significant issue in the field of high-temperature structural integrity. In this paper, the creep rupture assessment of 3D pressure pipelines with volumetric defects subjected to cyclic thermo-mechanical loadings is done using a direct numerical approach within the framework of stress compensation method (SCM). For calculation of creep rupture limit, an extended shakedown analysis scheme with yield strength correction is essentially performed, where the revised yield strength is determined as the minimum of the plastic yield strength and the creep rupture strength of material corresponding to a specified elevated temperature and rupture time. This direct numerical approach performs the creep rupture assessment by using the given creep rupture data of material rather than simulating the degenerative process of material based on creep damage constitutive equations under a specified loading history. The numerical approach is incorporated into commercial finite element software of Abaqus. Parametric studies on geometric dimensions of part-through slot affecting the creep rupture limit of 3D pressure pipelines with volumetric defects are conducted. Numerical results shown in this study indicate that the direct numerical approach accurately identifies the creep rupture limit boundary of the pressure pipeline, verified by the elastic-plastic cycle-by-cycle analysis. Failure mechanisms, such as local creep rupture, global creep rupture and global plastic rupture are detected under different loading combinations. These results give the helpful information for in-service integrity assessment of defective pressure pipelines at elevated temperature, and demonstrate the applicability and application prospect of the direct numerical approach in solving questions relevant to design or life assessment of other engineering structures.

CCG of PE100 and Life Prediction of PE Pipe With Axial Semi-Elliptical Crack

Viscoelastic and Damage Model of Polyethylene Pipe Material for Slow Crack Growth Analysis

Investigation On Creep-Rupture Failure Time Of Hdpe Pipe Under Hydrostatic Pressure

Prediction of Ductile Rupture Failure Life of HDPE Pipe

Probabilistic model to predict longitudinal fracture failure of buried pvc pipes

Experimental and Numerical Investigation on the Seismic Behavior of above Ground High Density Polyethylene Pipe in Nuclear Power Plant

Fatigue crack growth and slow crack growth of HDPE pipes under internal pressure and flat plate compression

Study on Viscoelastic Behavior During Slow Crack Growth of Medium Density Polyethylene Pipes

Mechanism of Slow Crack Growth in Polyethylene: A Finite Element Approach

Creep Crack Growth Prediction and Assessment Incorporating Constraint Effect for Pressurized Pipes with Axial Surface Cracks

A Creep Crack Growth Life Assessment Method for Pressurized Pipes Based on a Two-Parameter Approach

Determination of material fracture toughness by a computational/experimental approach for rapid crack propagation in PE pipe

Prediction of Creep Crack Initiation Behavior Considering Constraint Effects for Cracked Pipes

Numerical Study on Dimensions and Orientation Effect of Semi-Elliptical Cracks in PE100 Pipelines

Creep Behaviors Calculated by Varying Material Constants Obtained from Different Stress Regions for a Closed-End P91 Pipe

Using J-integral analysis to predict the failure of HDPE pipes under crack face load and internal pressure

Quantitative Assessment of Damage in Buried Polyethylene Pipe Subjected to Land Subsidence

Material Fracture Toughness Determination for Polyethylene Pipe Materials Using Small Scale Test Results

The performance and causes of failure of polyethylene pipes subjected to constant and fluctuating internal pressure loadings

Creep Rupture Assessment of Cyclically Heated 3D Pressure Pipelines with Volumetric Defects Using a Direct Numerical Approach

Study of Mode I-II Mixed Crack Propagation in Electrofusion Joint of Polyethylene Pipe