Abstract:The 2195 Al-Li alloy, as one of the representative third-generation Al-Li alloys, has extensive applications in lightweight aerospace structures. In this paper, the anisotropy in mechanical properties and microstructure evolution of 2195 Al-Li alloy sheets were investigated under a strain rate of 0.01, 0.1, 1 s-1 and a temperature of 440 and 500 °C. Experimental results showed that the hot tensile properties of the 2195 Al-Li alloy sheet exhibited a strong dependence on loading directions. The peak stress (PS) and elongation (EL) along the rolling direction (RD) were larger than the transverse direction (TD). For the tests carried out at 440 °C-1 s-1, the PS values of the sheets stretched along the RD and TD are 142.9 MPa and 110.2 MPa, respectively. And, most of the PS anisotropy values are larger than 15%. The anisotropy in EL is less significant than in PS. All the differences are about 10%. Moreover, dimples in the samples stretched along RD were more and deeper than those along TD at 440 °C. The fracture morphology along RD and TD were similar, and both were cleavage fractures at 500 °C. Particularly, the fractions of high angle grain boundaries (HAGBs) along TD were all about 5% larger than those of RD. And, there were more small-sized continuous dynamic recrystallization (CDRX) grains inside the initial grains and discontinuous dynamic recrystallization (DDRX) grains featured with the local bulge of grain boundaries along TD. This was due to the smaller average Schmid factor and the vertical EL trend of the initial grains when the samples were stretched along TD. A model of grain evolution during the dynamic recrystallization (DRX) along RD and TD was proposed based on EBSD results. The Schmid factor and banded structure had a more prominent effect on the hot ductility of the 2195 Al-Li alloy compared with the degree of DRX, thus presenting a higher EL and better hot ductility along RD.

High- and Low-Temperature Deformation Behavior of Different Orientation Hot-Rolled Annealed Zircaloy-4

Deformation mechanism, orientation evolution and mechanical properties of annealed cross-rolled Mg-Zn-Zr-Y-Gd sheet during tension

Texture development and mechanical behavior of Zircaloy-4 alloy plates fabricated by cold rolling and annealing

Microstructures and Mechanical Properties of a Commercial Pure Zirconium during Rolling and Annealing at Different Temperatures

Effect of cold rolling on microstructure and mechanical properties of pure Zr

Effect of uniaxial loading direction on mechanical responses and texture evolution in cold pilgered Zircaloy-4 tube: Experiments and modeling

Hot deformation behaviour of Zircaloy-4 at varying strain rate and its microstructural evolution

Tensile fracture behavior and texture evolution of a hot-rolled W-Y<sub>2</sub>(Zr)O<sub>3</sub> alloy

Annealing Behavior of Nanostructured Aluminum Produced by Cold Rolling to Ultrahigh Strains

MICROSTRUCTURES AND BOUNDARY DISTRIBUTIONS IN Al POLYCRYSTALS ROLLED AT DIFFERENT TEMPERATURES

Tensile fracture behavior and texture evolution of a hot-rolled W–Y2(Zr)O3 alloy

Effect of heating rate on the recrystallization behavior and mechanical properties of a cold-rolled Zr702

Understanding the Mechanism for the In-Plane Yielding Anisotropy of a Hot-Rolled Zirconium Plate

Effect of Initial Orientation on the Anisotropy in Microstructure and Mechanical Properties of 2195 Al-Li Alloy Sheet during Hot Tensile Deformation

Microstructure, texture evolution and mechanical anisotropy of Mg-Gd-Y-Zn-Zr alloy sheets produced by unidirectional and cross rolling

Evolution of Shear Bands in the Structure of a Zirconium-Based Amorphous Alloy during Rolling at Different Temperatures

In-situ EBSD analysis of hydride phase transformation and its effect on micromechanical behavior in Zircaloy-4 under uniaxial tensile loading

Revealing the evolution mechanisms of microstructure, texture and mechanical behavior in Zr702 alloy plates fabricated by accumulative roll bonding

Deformation And Annealing Textures Of Extruded And Cold Rolled Pure Ni Single Crystals Of Cube Orientation

Effect of cryogenic rolling on the microstructure and texture of CuCrZr alloy

Hot Deformation Behavior and Microstructure Evolution of High-Strength Al-Zn-Mg-Cu Alloy