Low-temperature sintered (Ti, Zr, Nb, Ta, Mo)C-based composites toughened with damage-free SiC w
Yang Liu,Liang Xu,Hua-Tay Lin,Weiming Guo,Shikuan Sun
DOI: https://doi.org/10.1016/j.jeurceramsoc.2022.11.051
IF: 5.7
2022-11-22
Journal of the European Ceramic Society
Abstract:The high sintering temperature would have a great tendency to damage the morphology and thus properties of the silicon carbide whisker (SiC w ) in high entropy carbide-silicon carbide whiskers (HEC-SiC w ) composites, which, in turn, would impact the effectiveness of the operative toughening mechanisms. The objective of this study was to achieve full contributions to the toughening effects of SiC w by preparing (Ti, Zr, Nb, Ta, Mo)C-SiC w composites at low temperature (1600 °C) using cobalt as additives. Results showed that the fracture toughness of the (Ti, Zr, Nb, Ta, Mo)C bulk reinforced with 20 vol.% SiC w and 5 vol.% Co was 7.2 MPa∙m 1/2 , which was much higher than that of the (Ti, Zr, Nb, Ta, Mo)C bulk only sintered with 5 vol.% Co (3.4 MPa∙m 1/2 ). Meanwhile, it was also higher than that of the reported HEC-20 vol.% SiC w composite sintered at 2000 °C (4.3 MPa∙m 1/2 ). For the fracture toughness of HEC-SiC w composites, it was significantly increased by the introduction of damage-free SiC w .
materials science, ceramics