Abstract:Nanoand microreinforcements such as carbon nanotubes (CNT), silicon carbide nanowires (SiCnw), and silicon carbide whisker (SiCw) with high strength and large surface area have great potentials applied to ceramic matrix composites (CMCs) in the following ways. With superior performances, these reinforcements can be used to CMCs individually, meanwhile, they can also be used to improve the interfacial properties of fiber reinforced CMCs for better performance. To overcome the challenge of poor dispersion quality of traditional CNT reinforced CMCs, in this work, various CNT assemblies were fabricated and applied to prepare their CMCs. SiCN ceramic matrix composites impregnated with multi-walled carbon nanotubes buckpapers (BP) were prepared by polymer impregnation pyrolysis (PIP). With 3 times PIP cycles, the composite showed complete and successful impregnation, and the obtained BP/SiCN composites showed excellent electrical conductivity of 185 S/cm, about 3 times higher than that of pure BP. CNT film (CNTf) prepared by floating catalyst method was used to prepare CNTf/SiC composite by chemical vapor infiltration (CVI) method. Test of mechanical properties indicates that CNTf/SiC composite showed excellent tensile strength of 713 MPa with 2 CVI cycles, about 21 times higher than that of pure CNTf. Electrical conductivity of CNTf/SiC composite was 350 S/cm with 1 CVI cycle, about 10 7 times higher than that of pure SiC ceramic. CNT/SiC produced by direct infiltration of SiC matrix into a porous vertically aligned CNT arrays have been demonstrated to possess Corresponding author. Tel.:+86-29-88495312; fax: +86-29-88494620. E-mail address: phdhuimei@yahoo.com (H. Mei) a unique microstructure and excellent micromechanical properties. The anisotropic compressive behavior of the composite was analyzed, and it was revealed that the longitudinal compressive strengths was 3 times higher than the transverse compressive strengths. An ice-segregation-induced self-assembly technique was employed to prepare CNT aerogel with well-defined macroporous architectures which was subsequently infiltrated with SiC matrix by 5 CVI cycles. The specimens exhibited lamellar structure with parallel lamellaes intersected at discrete angles. By observing, there are in fact five different representative anisotropic macrostructures of the composite. The compressive strengths of these five different loading modes with respect to lamella orientation were tested respectively, and the failure mechanisms were attributed to the anisotropic nature of the macrostructures. Porous SiCnw/SiC ceramic matrix composite with macroscopic unidirectionally aligned channels was also prepared by ice-segregation-induced self-assembly combined with CVI method. Flexural and compressive strengths of the composite with different CVI cycles were tested, and the results indicated an anisotropy of the composite. With 7 CVI cycles, transverse compression strengths of the composite was about 3.5 times higher than the longitudinal compression strengths. Introducing nanoand microreinforcements into the interfaces of C/SiC composites will improve the performances of the composite efficiently. CNT-C/SiC composites were prepared via CVI combined with electrophoretic deposition (EPD) methodology which enables CNT-coating of reinforcing fibers at varying load fractions. It was found that as increase of CNT quantity during electrodeposition, tensile strength of CNT-C/SiC increased substantially by 10.7%, 39.3%, and 45.2% corresponding to the CNT deposition times of 5, 8, and 10 minutes, respectively. For the same EPD periods, work of fracture increased by 49.4%, 82.7%, 120.8%. The electromagnetic interference absorption shielding effectiveness of the CNT-C/SiC composites was also found to increase significantly with EPD duration, and it increased by 56.5% over C/SiC composites at an EPD duration of 10 min. The strength of C/SiC reinforced with 5 wt% and 15 wt% SiCw brushed on the carbon fiber cloth increased by 98.5% and 64.3%, respectively.

Strengthening and Toughening Effects of MWCNTs on Si2BC3N Ceramics Sintered by SPS Technique

Enhanced Thermal Shock and Oxidation Resistance of Si2BC3N Ceramics Through MWCNTs Incorporation

Enhanced Mechanical Properties and Thermal Shock Resistance of Si2BC3N Ceramics with SiC Coated MWCNTs

The Effect of CNTs on the Spark Plasma Sintering Densification Behavior and Mechanical Properties of B4C-Si Powders

The Enhanced Mechanical Properties of SiC Nanowires/ba 0.75sr 0.25al 2si 2O 8 Ceramics with Embedded SiO 2 Interface

Preparation and characterization of high hard and high tough ultrafine WC ceramics containing hybrid graphene and SiC nanowire

Effects of Ti on the Microstructural Evolution and Mechanical Property of the SiBCN-Ti Composite Ceramics

Preparation and mechanical properties of SiCw-reinforced WC-10Ni3Al cemented carbide by microwave sintering

The Enhanced Mechanical Properties of SiC Nanowires/ba0.75sr0.25al2si2o8 Ceramics with Embedded SiO2 Interface

Effect of Nano SiC on Microstructure and Mechanical Properties of BN-ZrO2-SiC Multiphase Ceramics

Mechanical properties and microstructure of laminated Si3N4+SiCw/BN+Al2O3 ceramics densified by spark plasma sintering

Potentials of nano- and micro- reinforcements applied to ceramic matrix composites

Effects of the addition of multi-walled carbon nanotubes on the microstructure and properties of Ti(C,N)-based cermets prepared by spark plasma sintering

Mechanical Properties of WC-Si3N4 Composites with Ultrafine Porous Boron Nitride Nanofiber Additive

Enhanced Mechanical Properties, Thermal Shock Resistance and Oxidation Resistance of Si2BC3N Ceramics with Zr-Al Addition

Processing and Characterization of SiB0.5C1.5N0.5 Produced by Mechanical Alloying and Subsequent Spark Plasma Sintering

New Route To Improve The Flexural Strength Of Silicon Nitride Ceramics By Introducing Tungsten Carbide Nanoparticles

Preparation and mechanical behaviors of multiscale SiC nanowires/carbon fiber reinforced silicon oxycarbide ceramic composites

Strengthening and toughening effect and its mechanism for Si3N4(p)/SiC(w)-MoSi2 composite

Processing and mechanical properties of B4C-SiCw ceramics densified by spark plasma sintering

MoSi2 Inter-Metallic Composites Reinforced and Toughened by CNTs