Abstract:Cf/SiC composites were prepared by polymeric precursor pyrolysis-hot pressing with AlN and Y2O3 as additives. The effects of sintering temperature and additives on the microstructures and mechanical properties of the composites were investigated. During sintering, Y2O3 reacted with the pyrolysis products from the PCS and the oxides on the surfaces of the AlN and SiC grains, forming a liquid-phase assisting the densification of the composites. So, in combination with SiC-AlN solid solution formed through a reaction–dissolution–precipitation process, the composite sintered at the temperature as low as 1750°C had showed higher density and better mechanical properties. The highest flexural strength and fracture toughness, 691.6 MPa and 20.7 MPa·m1/2, respectively, were obtained at the composite sintered at 1800°C. This could be explained by desirable fiber/matrix interfacial bonding resulting from the formation of the carbon-rich fiber/matrix interphase containing a certain number of SiC-AlN solid solution grains. In spite of a tough-like failure mode, the composite sintered at 1700°C exhibited much lower mechanical properties, which was attributed to that the fiber/matrix interfacial bonding was too weak to effectively transfer load from matrix to fibers. And the composite sintered at temperatures above 1850°C displayed brittle behavior because of the strongly bonded fiber/matrix interfaces as well as degradation of the fibers.

Effect of Fiber Content on Mechanical Property and Fracture Mechanisms of Cf/SiC Composites

Microstructures and Interface of C2/SiC Composites

The Effect of Sintering Additive on Fracture Behavior of Carbon-Whisker-reinforced Silicon Carbide Composites

Mechanical Properties and Interfaces of Cf/SiC Composites

Behavior of Short Carbon Fibers in Cfiber/Si3N4 Composites by Hot Pressed Sintering

Effect of Fiber Characteristics on Fracture Behavior of C F /sic Composites

Effect of Carbon Particle and Carbon Fiber on the Microstructure and Mechanical Properties of Short Fiber Reinforced Reaction Bonded Silicon Carbide Composite

Improved Mechanical Properties of Csf/SiC Composite by Rapid Hot Press Sintering

Influence of Sintering Process on the Fracture Behavior of C-F/SiC Laminated Ceramic Composites

Mechanical properties of C/C-SiC composites by compression molding

Behavior of Short Carbon Fibers in C<sub>fiber</sub>/Si<sub>3</sub>N<sub>4</sub> Composites by Hot Pressed Sintering

The Effect of Annealing Temperature on Micro-Structure and Mechanical Properties of C/Sic Composites

Effect of In-situ SiC Particle on Room-temperature Fracture Toughness of SiCP/MoSi2

Effects of Random Chopped Fiber on the Flexural Strength and Toughness of Reaction Bonded Silicon Carbide Composite

Effect of Sintering Additive Composition on the Mechanical and Tribological Properties of Si3n4/Sic Ceramics

Effects of fiber dispersion on mechanical properties of C/C-SiC composites

Effects of Adding Methods of YAG on Sintering Behaviour, Mechanical Properties and Microstructure of SiC Ceramic

Influence of Short Carbon Fiber Content on Mechanical and Dielectric Properties of C-Fiber/Si3n4 Composites

Effect of Fiber Dispersion on Compression Performance of C/C-SiC Composites

Effect of SiC content on properties of reaction sintered SiC-Si3N4 composites

Microstructures and mechanical properties of Cf/SiC composites by precursor pyrolysis-hot pressing