Abstract:Cf/SiC composites were prepared by polymeric precursor pyrolysis-hot pressing with AlN and Y2O3 as additives. The effects of sintering temperature and additives on the microstructures and mechanical properties of the composites were investigated. During sintering, Y2O3 reacted with the pyrolysis products from the PCS and the oxides on the surfaces of the AlN and SiC grains, forming a liquid-phase assisting the densification of the composites. So, in combination with SiC-AlN solid solution formed through a reaction–dissolution–precipitation process, the composite sintered at the temperature as low as 1750°C had showed higher density and better mechanical properties. The highest flexural strength and fracture toughness, 691.6 MPa and 20.7 MPa·m1/2, respectively, were obtained at the composite sintered at 1800°C. This could be explained by desirable fiber/matrix interfacial bonding resulting from the formation of the carbon-rich fiber/matrix interphase containing a certain number of SiC-AlN solid solution grains. In spite of a tough-like failure mode, the composite sintered at 1700°C exhibited much lower mechanical properties, which was attributed to that the fiber/matrix interfacial bonding was too weak to effectively transfer load from matrix to fibers. And the composite sintered at temperatures above 1850°C displayed brittle behavior because of the strongly bonded fiber/matrix interfaces as well as degradation of the fibers.

Microstructures and mechanical properties of Cf/SiC composites by precursor pyrolysis-hot pressing

Microstructures of a carbon-fiber-reinforced silicon-carbide composite produced by precursor pyrolysis and hot pressing

Mechanical Properties and Interfaces of Cf/SiC Composites

Microstructures of Short-Carbon-Fiber-Reinforced Sic Composites Prepared by Hot-Pressing

Microstructures and Interface of C2/SiC Composites

Influence of pyrolytic carbon interphase and pyrolysis temperature on the mechanical and tribological properties of Cf/SiC after heat treatment at 1800 °C

Slurry‐impregnating hot‐press sintered silicon carbide nanofiber/silicon carbide composites with Al‐B‐C as sintering additives

Effect of polycarbosilane content on microstructures and mechanical properties of short-carbon-fibre-reinforced SiC composites

Effect of sintering temperature and holding time on the microstructure and mechanical properties of ZrB2–SiCw composites

Microstructure and Mechanical Properties of Hot-Pressed Al2O3–mullite–ZrO2–SiC Composites

Structure and properties of fine diameter continuous SiC ceramic fiber reinforced Al matrix composites

Synthesis of α-SiC/α-SiAlON composites by spark plasma sintering: Phase formation and microstructures development

Pressureless Sintering and High-Temperature Strength of SiC-AlN Ceramics

The Effect of Annealing Temperature on Micro-Structure and Mechanical Properties of C/Sic Composites

Effect of Fiber Characteristics on Fracture Behavior of C F /sic Composites

Study on Zrc-20vol.%Sicw Ultrahigh Temperature Ceramics by Hot Pressing

Improved Mechanical Properties of Csf/SiC Composite by Rapid Hot Press Sintering

Fabrication, Microstructure, and Properties of SiC/Al 4 SiC 4 Multiphase Ceramics Via an In-Situ Formed Liquid Phase Sintering

Effect of Fiber Content on Mechanical Property and Fracture Mechanisms of Cf/SiC Composites

Characterization and mechanical properties of Cf/ZrB2-SiC composites fabricated by a hybrid technique based on slurry impregnation, polymer infiltration and pyrolysis and low-temperature hot pressing

Effect of Pyrocarbon Content in C/C Preforms on Microstructure and Mechanical Properties of the C/C–SiC Composites