Abstract:Features peculiar to the synthesis of SiC–Si 3 N 4 –Si 2 N 2 O composite powder with a controlled content of silicon carbide, nitride, and oxynitride phases, as well as the structure and properties of hot-pressed ceramics produced from this powder, were examined. The optimal composition of the synthesized SiC–Si 3 N 4 –Si 2 N 2 O powder was achieved by heating a 1 : 3 mixture of thermally expanded graphite (TEG) and silicon up to 1200°C in air. The interaction of TEG with fine silicon at 1200°C led to the formation of a solid solution of carbon in silicon carbide, accompanied by heat release. The generated heat increased temperature within localized volumes of the TEG cellular structure to a level where air nitrogen facilitated the development of silicon nitride and oxynitride and an amorphous phase. The amorphous phase crystallized as the interaction time increased to 2.5 h. The duration of the process influenced the final distribution of the phases, formed with the participation of CO, SiO, and air nitrogen. The microstructure of the synthesized powder was characterized by a general agglomerated state, resulting from rod and plate forms of Si 3 N 4 and Si 2 N 2 O. Hot pressing of the synthesized SiC–Si 3 N 4 –Si 2 N 2 O composite powder with Al 2 O 3 and Y 2 O 3 activators yielded superfine ceramics, possessing enhanced hardness and fracture toughness (HV10 = 20.7 GPa and K Ic = 6.5 MPa · m 1/2 ). The structure of the ceramics sintered at 2000°C differed from those sintered at 1850°C, primarily by higher density and average grain size. The superfine state significantly influenced the abrasive wear resistance of the ceramics in dry friction conditions. The linear wear index of a sample with an average size of structural elements varying from 0.2 to 1.5 μm was 111 μm/km at a sliding speed of 1 m/sec under a load of 0.2 MPa. This was significantly lower than the linear wear index of industrial ceramics of reaction-sintered silicon carbide (RSSC), which was 232.4 μm/km.

Microstructures of Short-Carbon-Fiber-Reinforced Sic Composites Prepared by Hot-Pressing

Effect of polycarbosilane content on microstructures and mechanical properties of short-carbon-fibre-reinforced SiC composites

Microstructures of a carbon-fiber-reinforced silicon-carbide composite produced by precursor pyrolysis and hot pressing

Microstructure of the Cf/SiC composites by precursor conversion-hot pressing sintering

Microstructures and mechanical properties of Cf/SiC composites by precursor pyrolysis-hot pressing

Hot-Pressed Al2o3-Sic(-C) Composites With Polycarbosilane As The Precursor

Hot-pressed A12O3–SiC(–C) composites with polycarbosilane as the precursor

Carbon-fiber-reinforced silicon carbide composites prepared by precursor pyrolysis-hot pressing

Microstructures and Thermophysical Properties of Polymer Derived SiC/C Composites

Microstructure and Mechanical Properties of Sicp/Mosi(2)Composites Manufactured by in Situ Reaction and Hot Pressing

Processing and Microstructure Characterization of Liquid-Phase-sintered, Α-Sic Matrix Composites

Microstructures and Interface of C2/SiC Composites

Mechanical properties of Al2O3–SiC–C composites using polycarbosilane as SiC precursor

Preparation and Properties of Short-Fiber-reinforced C/SiC Composites

Structure Formation in Silicon Carbide–Alumina Composites during Electroconsolidation

Study on the Performance for Silicon Carbide Ceramics by Hot-pressing Sintering

The Effect of Annealing Temperature on Micro-Structure and Mechanical Properties of C/Sic Composites

Synthesis and Consolidation of Composite Materials in the SiC–Si3N4–Si2N2O System

Fabrication, Microstructure and Mechanical Properties of Silicon Carbide Short Fiber/Si3N4p-Reinforced BAS composites

Silicon Carbide/Polysilazane Composite: Effect of Temperature on the Densification, Phase, and Microstructure Evolution

Microstructures and Mechanical Properties of Hot-Pressed -Matrix Composites Reinforced with SiC and Particles