Abstract:Si3N4/SiC composites containing 0-30 vol% SiC were fabricated by pressureless sintering and sinter-post-HIPing method using fine Si3N4 and nano-sized SiC powders. Specimens reached full density (>96% theoretical density (th. d.)) except the composites made by pressureless sintering which contained a small amount of sintering additives or a large amount of SiC. All composites with 10 mass% sintering additives reached full density (similar to 99% th. d.) by sinter-post-HIPing. The addition of SiC particles greatly influenced the grain morphology of the Si3N4 matrix. The average grain thickness, length and aspect ratio decreased with increasing SiC content because of grain boundary pinning by SiC particles. Also the mechanical properties were markedly dependent upon the fraction of SiC particle reinforcement, as well as matrix grain size and porosity. When the materials were pressureless sintered, the strength of the composite increased with SiC additions below 20 vol%. Further increase in the SIC content resulted in a corresponding decrease in strength. Maximum strength of 1150 MPa was attained at 20 vol% SiC addition. The increase in strength by addition of SiC is due to decrease of grain size of Si3N4 matrix grain size, and the decrease by further increase in SiC content is caused by porosity and SiC agglomerate. On the other hand, toughness decreased monotonically with SiC content. The strength of all samples was enhanced by sinter-post-HIPing without any change in fracture toughness. The strength of sintered samples with 10-15 vol% SiC increased by similar to 20% to 1260 MPa by post-HIPing. The increase in strength by post-HIPing was interpreted as being due to a decrease flaw size.

Preparation and Properties of Short-Fiber-reinforced C/SiC Composites

Tribological Properties of Carbon Fiber Toughened SiC Prepared by Hot Pressing Sintering

Improved Mechanical Properties of Csf/SiC Composite by Rapid Hot Press Sintering

Oxidation Kinetics and Its Impact on the Strength of Carbon Short Fiber Reinforced C/SiC Ceramics

Microstructures of Short-Carbon-Fiber-Reinforced Sic Composites Prepared by Hot-Pressing

Fabrication of C/SiC composites by siliconizing carbon fiber reinforced nanoporous carbon matrix preforms and their properties

Mechanical Properties and Interfaces of Cf/SiC Composites

Oxidation behavior of 3D SiCf/SiBCN composites at 800–1200 °C

Mechanical and Oxidation Properties of C/SiC Corrugated Lattice Core Composite Sandwich Panels

High-temperature tensile behavior of 3D SiC/SiC composites

Long-term oxidation and ablation behavior of C<sub>f</sub>/ZrB<sub>2</sub>-SiC composites at 1500, 2000, and 2200C

Characterization of hot-pressed short carbon fiber reinforced ZrB2–SiC ultra-high temperature ceramic composites

Microstructure and mechanical properties of short-carbon-fiber/Ti3SiC2 composites

Fabrication and Mechanical Properties of Si3N4/SiC Nanocompoisites under Pressureless Sintering.

Structure and properties of fine diameter continuous SiC ceramic fiber reinforced Al matrix composites

Influence of Oxidation Damages on Mechanical Properties of SiC/SiC Composite Using Domestic Hi-Nicalon Type SiC Fibers

Mechanical properties and strengthening mechanism of SiCf/SiC mini-composites modified by SiC nanowires

Effects of chopped carbon fiber on the forming, structure and mechanical properties of CCF/SiC composites fabricated by SLS and RMI

Microstructure and Mechanical Properties of SiC F /sibcn Ceramic Matrix Composites

Oxidation behaviors of carbon fiber reinforced multilayer SiC-Si3N4 matrix composites

Fabrication and Mechanical Properties of Si3n4/Sic Nanocomposite with Pressureless Sintering and Sinter-Post-Hiping