Abstract:Carbon-fiber-reinforced carbon-silicon carbide (C/C-SiC) composites were prepared by impregnating carbon fibers with ethynylphenyl-terminated poly(silylene-acetylene) (EPTSA) as a single-source precursor with subsequent hot pressing and pyrolysis. The structural evolution, crystallization behavior, and graphitization of bulk C-SiC ceramics, as well as their mechanical properties and ablation behavior, were investigated. The EPTSA precursor starts to transform into inorganic SiC ceramic materials at 800 degrees C, which is characterized by an amorphous structure with weight loss, shrinkage, and densification between 800 and 1000 degrees C. The formation of SiC crystals inhibited the growth of the graphitic structure between 1000 and 1200 degrees C. As the temperature was raised, both graphite and SiC crystals continued to grow, and the crystalline forms became more complete. The carbon-fiber cloth (T300CF)-reinforced C-SiC composite (T300CF/C-SiC) prepared using polymer infiltration and pyrolysis (PIP) exhibited excellent mechanical properties. After five PIP cycles, the flexural strength, flexural modulus, and interlaminar shear strength of the T300CF/C-SiC composite reached 169 MPa, 32.5 GPa, and 9.38 MPa, respectively. In addition, the chopped-carbon-fiber-reinforced C-SiC composite fabricated using the PIP process demonstrated good oxyacetylene-torch ablation properties.

Carbon-fiber-reinforced silicon carbide composites prepared by precursor pyrolysis-hot pressing

Microstructures of a carbon-fiber-reinforced silicon-carbide composite produced by precursor pyrolysis and hot pressing

Mechanical Properties and Interfaces of Cf/SiC Composites

Microstructures of Short-Carbon-Fiber-Reinforced Sic Composites Prepared by Hot-Pressing

Slurry‐impregnating hot‐press sintered silicon carbide nanofiber/silicon carbide composites with Al‐B‐C as sintering additives

Effect of Pyrocarbon Content in C/C Preforms on Microstructure and Mechanical Properties of the C/C–SiC Composites

Improved Mechanical Properties of Csf/SiC Composite by Rapid Hot Press Sintering

Tribological Properties of Carbon Fiber Toughened SiC Prepared by Hot Pressing Sintering

Influence of pyrolytic carbon interphase and pyrolysis temperature on the mechanical and tribological properties of Cf/SiC after heat treatment at 1800 °C

Preceramic Paper-Derived SiCf/SiCp Composites Obtained by Spark Plasma Sintering: Processing, Microstructure and Mechanical Properties

Structure and properties of fine diameter continuous SiC ceramic fiber reinforced Al matrix composites

Effect of pyrolysis temperatures on the performance of SiCf/SiC composites

Study on the Performance for Silicon Carbide Ceramics by Hot-pressing Sintering

Effect of chemical vapor infiltration on the flexural properties of C/C-SiC composites prepared by the precursor infiltration pyrolysis method

C/C–SiC Composites Derived from Single‐source Poly(silylene–acetylene) Precursors

Effect of polycarbosilane content on microstructures and mechanical properties of short-carbon-fibre-reinforced SiC composites

Microstructures and Interface of C2/SiC Composites

Effect of sintering temperature and holding time on the microstructure and mechanical properties of ZrB2–SiCw composites

Preparation and Characterization of High-Performance ZrB 2 –sic–cf Composites Sintered at 1450 °C

Effect of Fiber Characteristics on Fracture Behavior of C F /sic Composites

Design and Optimization of the Coating Thickness on Chopped Carbon Fibers and Sintering Temperature for ZrB2-SiC-C-f Composites Prepared by Hot Pressing