Abstract:Arrays of randomly oriented zinc oxide (ZnO) nanowires were fabricated on silicon wafers via a simple thermal evaporation method. During the fabrication, the temperature around the substrate was below 500°C. The products were analyzed by conventional means and determined to be single crystals of wurtzite-type ZnO that grew along the c-axis. These nanowires were 10–100nm in diameter and 10–100μm in length, suggesting a possible high field enhancement factor. The dependence of the field emission current on the anode–cathode voltage (I–V behavior) of the ZnO nanowire arrays was measured in a lab-built ultrahigh vacuum system with a base pressure of 10−7Pa. After surface cleaning by heat treatment, two characteristic electric fields, under which 10μA/cm2 and 1mA/cm2 current densities were extracted, were measured to be 4.0 and 4.7V/μm, respectively. As observed with a transparent anode, emission occurred uniformly over the whole sample surface. A 72h-long test on emission stability was performed under a constant voltage of 2.75kV. The current dropped occasionally to approximately 80% of the initial value during the test owing to the poor adherence of the nanowires to the substrate. These preliminary results have shown the perspective of, as well as a major drawback to, a ZnO nanowire array being developed into a cold electron source to be used in future electronic devices.

Preparation of ZnO Nanowires for High Emission Current Field Emitter Arrays

Fabrication of Large-Area ZnO Nanowire Field Emitter Arrays by Thermal Oxidation for High-Current Application

Precisely-controlled Fabrication of Single ZnO Nanoemitter Arrays and Their Possible Application in Low Energy Parallel Electron Beam Exposure.

Controlled Preparation of Micron-Size-Pattemed ZnO Nanowire Field Emitters

ZnO Nanowire Field Emitter Arrays: Fabrication, Field Emission Mechanism and Applications

Field Emission Properties of Zinc Oxide Nanowires Fabricated by Thermal Evaporation

Field Emission from Nonaligned Zinc Oxide Nanowires

Field Emission Properties of ZnO Nanowire Array Directly Grown from Zinc Substrate

Large-Scale Synthesis of Bicrystalline ZnO Nanowire Arrays by Thermal Oxidation of Zinc Film: Growth Mechanism and High-Performance Field Emission

Fabrication Of Zno Nanowire Field Emitter Arrays For Field Emission Display Application

Fabrication of ZnO Nanowires by Vapor-Phase Deposition and Their Field Emission Properties

Field Emission and Optical Properties of ZnO Nanowires Grown Directly on Conducting Brass Substrates.

Patterned Growth and Field Emission Properties of ZnO Nanowires Prepared by Thermal Oxidation Method

Optimizing the Field Emission Properties of ZnO Nanowire Arrays by Precisely Tuning the Population Density and Application in Large-Area Gated Field Emitter Arrays.

Stable, Self-Ballasting Field Emission from Zinc Oxide Nanowires Grown on an Array of Vertically Aligned Carbon Nanofibers

Fabrication and Characterization of Gated ZnO Nanowire Field Electron Emitters

Field Emission from Zinc Oxide Nanostructures and Its Degradation

Field Emission from Oxide Nanowires: Mechanism and Applications

Fabrication of Gated ZnO Nanowire Field Emitter Arrays for Pulsed Flat Panel X-ray Source

Field Emission Microscopy Study of Zinc Oxide Nanowires on Tungsten Tip

Zno Nanowire Field Electron Emitters