Abstract:A novel hierarchical zinc oxide three-dimensional architecture of densely packed and well-aligned bilayer ZnO nanowire arrays was synthesized via a hydrothermal process. For ZnO nanowire growth, a layer of dense zinc microplatelet arrays was first obtained on copper foil by an electroplating method. Uniform ZnO nanowires were grown vertically on both surfaces of zinc microplatelet in hydrothermal solution only containing ammonia water. The obtained ZnO nanowire arrays possessed high packing density and uniform size, demonstrating a rapid nucleation and growth process in the initial stage of growth. But then Ostwald ripening dominated the morphology evolution of hierarchical ZnO architecture due to a low degree of supersaturation of ZnO. XRD and HRTEM characterizations confirmed ZnO possessing a highly crystalline nature with preferential (002) orientations along the c-axis direction. With the decrease of ZnO nanowire size, the absorption spectra of hierarchical ZnO film exhibited an increase of visible light absorption and slight red-shift of band gap, whereas its emission spectra exhibited a decrease of photoluminescence intensity, which can be ascribed to the increase of defects in ZnO structure with size decrease. The photocatalytic experiment indicated that the hierarchical nanostructure film had superior photocatalytic performance in the degradation of methyl orange solution under ultraviolet irradiation. The work also presented a simple approach for further practical application of ZnO nanowire arrays to nanoscale optoelectronic device.

Large-Scale Synthesis of Bicrystalline ZnO Nanowire Arrays by Thermal Oxidation of Zinc Film: Growth Mechanism and High-Performance Field Emission

Controllable Preparation of 1-D and Dendritic ZnO Nanowires and Their Large Area Field-Emission Properties

Synthesis of bilayer ZnO nanowire arrays: Morphology evolution, optical properties and photocatalytic performance

Direct Growth of Quasi-Aligned Ultrafine ZnS Nanowire Arrays on Conducting Zinc Foils and Their Field Emission Properties

Fabrication of Large-Area ZnO Nanowire Field Emitter Arrays by Thermal Oxidation for High-Current Application

Field Emission from Zinc Oxide Nanostructures and Its Degradation

Field Emission from Randomly Oriented Zno Nanowires

A Low-Temperature Aqueous Solution Route to Large-Scale Growth of Zno Nanowire Arrays

Studies on the Synthesis and Growth Mechanism of Single Crystal ZnO Nanowires

Field Emission Properties of ZnO Nanowire Array Directly Grown from Zinc Substrate

Reparation of ZnO Nanowires and Their Field Emission Properties

Field Emission and Optical Properties of ZnO Nanowires Grown Directly on Conducting Brass Substrates.

Uniform ZnO Nanowire Arrays: Hydrothermal Synthesis, Formation Mechanism and Field Emission Performance

Morphology-dependent Field Emission Properties and Wetting Behavior of ZnO Nanowire Arrays

Large-Scale and Rapid Synthesis of Ultralong ZnO Nanowire Films via Anodization

Catalyst-free Synthesis of ZnO Nanowire Arrays on Zinc Substrate by Low Temperature Thermal Oxidation

Patterned Growth and Field Emission of ZnO Nanowires

Growth mechanism and diameter control of well-aligned small-diameter ZnO nanowire arrays synthesized by a catalyst-free thermal evaporation method.

Controlled Preparation of Micron-Size-Pattemed ZnO Nanowire Field Emitters

Synthesis and photoluminescence properties of single crystal ZnO nanowires by thermal evaporation

Synthesis and Efficient Field Emission Characteristics of Patterned ZnO Nanowires