Abstract:Objectives: The aim of this study was to evaluate the mechanical properties and the subcritical crack growth behavior of a presintered dental Y-TZP (Kavo Everest ZS) and a hot isostatic pressed Y-TZP (Kavo Everest ZH) and to perform life data analysis. Methods: For each material 150 bending bars were produced. The initial fracture strength was determined in a four-point bending test. The subcritical crack growth parameters n and A were determined in a dynamic fatigue method at four decreasing loading rates from 110MPa/s to 0.11MPa/s in distilled water at 38°C. For each loading rate Weibull statistics were performed and the Weibull moduli m and characteristic strengths σ(0) were calculated. Using these data, strength-fracture probability-life time (SPT) predictions were derived for 1 day, 1 year, 5 years and 10 years, based on a static crack growth mechanism. Results: The "hipped" Y-TZP ceramic exhibited a higher initial strength (σ(c)=1618.18), characteristic strength (σ(0)=837.15) and fracture toughness (K(IC)=4.52MPa/m(1/2)) than the pre-sintered ceramic (σ(c)=1431, σ(0)=745.46 and K(IC)=3.17MPa/m(1/2), respectively). Fatigue parameters, n and A, were 28.5 and 7.97×10(-24) for Everest ZH and 30.15 and 5.47×10(-20) for Everest ZS. The predicted fracture stress at 5% failure probability for a lifetime of 10 years was 259.34MPa for Everest ZH and 263.2MPa for Everest ZS. Conclusions: Although the "hipped" Y-TZP showed favorable initial mechanical properties, no significant difference could be found in the susceptibility of both ceramics to subcritical crack growth and their long-term strength.

Determination of Fracture Toughness of Y-TZP Ceramics

Determination of Fracture Toughness of Zirconia Ceramics with Different Yttria Concentrations by SEVNB Method

Fracture Toughness of 3Y‐TZP Ceramic Determined by Modified SCF Method Based on Femtosecond Laser

Effect of Notch Depth on Fracture Toughness of Y-Tzp and Determination of Its Actual Value

Load‐deflection Behavior of Fracture Toughness Testing of Ceramics by SEVNB Method

Evaluation of Fracture Toughness of Zirconia Ceramics with Heterogeneous Yttrium Distribution Microstructures

Effect of notch depth on fracture toughness of zirconia ceramics tested by SEVNB method

SEVNB Method on Fracture Toughness of Ceramic

Effect of Molten Zone Ablated by Femtosecond Laser on Fracture Toughness of Oxide Ceramics

On the feasibility of the Chevron Notch Beam method to measure fracture toughness of fine-grained zirconia ceramics

The Effect of Groove and Notch Tip Angles on Testing Fracture Toughness by SEVNB Method: Models and Experimental Validation

Accurate measurement of fracture toughness in structural ceramics

Assessing fracture toughness in sintered Al2O3–ZrO2(3Y)–SiC ceramic composites through indentation technique

Reliable evaluation of fracture toughness in ceramics via nanosecond laser notching method

Evaluations on Ceramic Fracture Toughness Measurement by Edge Chipping

Microstructures and Mechanical Properties of Sr2Nb2O7-toughened 3Y-TZP Ceramics

Study of the Fracture Behavior of Tetragonal Zirconia Polycrystal with a Modified Phase Field Model

Subcritical crack growth behavior and life data analysis of two types of dental Y-TZP ceramics

Fracture Toughness of Advanced Structural Ceramics: Applying ASTM C1421

High Temperature Fracture Toughness and Residual Stress in Thermal Barrier Coatings Evaluated by an In-Situ Indentation Method

Zirconia-based Nanocomposite Toughened by Functionalized Multi-Wall Carbon Nanotubes