Abstract:Utilizing MgO as the precursor and deionized water as the solvent, this study synthesized nanoparticles of Mg(OH)2 via hydrothermal methods, aiming to control its purity, particle size, and morphology by understanding its growth under non-uniform nucleation. Characterization of crystal morphology and structure was conducted through scanning electron microscopy and X-ray diffraction, while laser particle size detection assessed the secondary particle size distribution. The study focused on how MgO's hydrothermal process conditions influence Mg(OH)2 crystal growth, particularly through ion concentration and release rate adjustments to direct crystal growth facets. These adjustments shifted the dominant growth plane, enhancing the peak intensity ratio I001/I101 from 1.03 to 2.14, thereby reducing surface polarity and secondary aggregation of crystals. The study of the physicochemical properties of the same sample at different times revealed the pattern of crystal dissolution and recrystallization. A 2 h hydrothermal reaction notably altered the particle size distribution, with a decrease in particles sized 0.2~0.4 μm and an increase in those sized 0.4~0.6 μm, alongside new particles over 1 μm, indicating a shift toward uniformity through dissolution and recrystallization. Optimal conditions (6% magnesium oxide concentration, 160 °C, 2 h) led to the synthesis of highly dispersed, uniformly sized magnesium hydroxide, showcasing a simple, eco-friendly, and high-yield process.

Fabrication of Tubular Magnesium Oxide Nanocrystals Via Combining Ammonium Sulfate Leaching and Precipitation Method and It's Crystal Growth Behavior

Fabrication of Y2O3-doped MgO Refractory Raw Materials Based on Magnesium Hydroxide from Salt-Lake Brine

Investigation of Crystallization Growth Characteristics of Mg(OH)2 Crystals under Unconstrained Conditions

MgO nanostructures synthesized by thermal evaporation

Preparation of Magnesia Nanoballs from Dolomite

Nanoscale magnesium hydroxide and magnesium oxide powders: Control over size, shape, and structure via hydrothermal synthesis

Preparation of Magnesium Hydroxide Chloride Hydrate Nanowires Using Calcined Dolomite

Formation of rod-like Mg(OH)2 nanocrystallites under hydrothermal conditions and the conversion to MgO nanorods by thermal dehydration

Synthesis of Magnesium Borate Nanorods by Sol-Gel Process

SYNTHESIS OF NANOMETER MAGNESIA BY SOL- GEL METHOD

Simple Synthesis of Single-crystalline Nanoplates of Magnesium Oxide

Large-scale synthesis of single-crystalline MgO with bone-like nanostructures

Preparation and Characterization of Magnesium Hydroxide Nanoparticles from Dolomite-Talc Ore

Synthesis and Characterization of Single Crystalline Mnooh and Mno2 Nanorods by Means of the Hydrothermal Process Assisted with Ctab

A simple solution calcination route to porous MgO nanoplates

Synthesis of High Surface Area Nanometer Magnesia by Solid-State Chemical Reaction

Synthesis of MgO Microspheres with Nanosheets in a Mechanical Force Reactor and Its Optical Property

Preparation of Ccalcining MgO and its precursor

Preparation and Crystallization Kinetics of Micron-Sized Mg(OH)2 in a Mixed Suspension Mixed Product Removal Crystallizer

Preparation of Nano-sized Magnesium Hydroxide from Dolomites by Acid Immersing

Study On The Growth Of Magnesium Hydroxide Crystals