Enhanced Stability and Thermoelectric Performance in Cu 1.85 Se-Based Compounds
Jing Jiang,Chengcheng Yang,Yi Niu,Jie Song,Chao Wang
DOI: https://doi.org/10.1021/acsami.1c08886
2021-07-30
Abstract:Liquid-like copper selenium compounds have attracted considerable interest in recent years for their excellent thermoelectric performance, abundant element reserves, and low toxicity. However, the related applications are still limited due to the phase transition and precipitation of Cu under an external field. Here, the cubic Cu1.85Se-based compounds with suppressed phase transition and improved critical voltage (Vc) are first studied. In particular, Li/Bi co-doping effectively optimizes hole concentration and the ZTs are substantially improved from 0.2 in Cu1.85Se to 0.7 in Li0.03Cu1.81Bi0.04Se at 760 K. Meanwhile, the latter shows an outstanding Vc above 0.22 V at 750 K, which is the highest value in Cu2–xSe thermoelectric compounds to date. Moreover, S is alloyed in Li0.03Cu1.81Bi0.04Se to greatly reduce the thermal conductivity and the ZT is further enhanced to 0.9 for Li0.03Cu1.81Bi0.04Se0.9S0.1 at 760 K. Our work sheds light on a new strategy to realize good stability and enhanced thermoelectric performance, which provides a new direction for further research.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acsami.1c08886.Temperature dependence of the thermoelectric properties of Cu1.8+xSe (x = 0, 0.03, 0.05, 0.06); XRD patterns of Cu1.8+xSe (x = 0, 0.03, 0.05, 0.06); XRD pattern of Li0.04Cu1.81Bi0.04Se and thermoelectric properties of LixCu1.85Se (x = 0, 0.01, 0.02, 0.03, 0.04); XPS spectra of Li0.03Cu1.81Bi0.04Se; high-temperature XRD patterns of Cu1.85Se and Li0.03Cu1.85Se; TGA analysis of Cu1.85Se and Li0.03Cu1.85Se; temperature dependence of Cu1.85–xSnxSe (x = 0, 0.01, 0.02, 0.03); temperature-dependent thermoelectric properties of Cu1.85–xBixSe (x = 0, 0.01, 0.02, 0.03, 0.04); temperature dependence of electrical thermal conductivity of LixCu1.85–xSe (x = 0, 0.01, 0.02, 0.03) and Li0.03Cu1.85–yBiySe (y = 0.02, 0.03, 0.04, 0.05); detailed calculation process of lattice thermal conductivity; high stability and reproducibility of the thermoelectric properties of Li0.03Cu1.81Bi0.04Se; temperature dependence of the thermoelectric properties of Li0.03Cu1.81Bi0.04Se1–zSz (z = 0, 0.05, 0.1, 0.2, 0.3); and temperature dependence of the electrical thermal conductivity for Cu1.85Se, Li0.03Cu1.85Se and Li0.03Cu1.81Bi0.04Se1–zSz (z = 0, 0.05, 0.1, 0.2, 0.3) (PDF)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology