Enhancement of the Thermoelectric Performance of Cu 2 GeSe 3 via Isoelectronic (Ag, S)-co-substitution

Zeqing Hu,Huihong Xu,Chen Yan,Yu Liu,Qinghua Han,Longjiu Cheng,Zhou Li,Jiming Song

DOI: https://doi.org/10.1021/acsami.2c02047

2022-04-29

Abstract:Recently, ternary Cu-based Cu-IV-Se (IV = Sb, Ge, and Sn) compounds have received extensive attention in the thermoelectric field. Compared with Cu-Sb-Se and Cu-Sn-Se, Cu-Ge-Se compounds have been less studied due to its poor Seebeck coefficient and high thermal conductivity. Here, the Cu₂GeSe₃ material with high electrical conductivity was first prepared, and then, its effective mass was increased by doping with S, which led to the Seebeck coefficient of the doped sample being 1.93 times higher than that of pristine Cu₂GeSe₃ at room temperature. Moreover, alloying Ag at the Cu site in the Cu₂GeSe_2.96S_0.04 sample could further cause a 5.16 times increase in the Seebeck coefficient at room temperature, and the lattice thermal conductivity was remarkably decreased because of the introduction of the dislocations in the Cu₂GeSe₃ sample. Finally, benefitted from the high Seebeck coefficient and low thermal conductivity, a record high <i>ZT</i> = 0.9 at 723 K was obtained for the Cu_1.85Ag_0.15GeSe_2.96S_0.04 sample, which increased 345% in comparison with the pristine Cu₂GeSe₃, and it is among the highest reported values for Cu₂GeSe₃-based thermoelectric.

materials science, multidisciplinary,nanoscience & nanotechnology