Abstract:WC-Co cemented carbides are widely used in the fields of military, aerospace, mining and cutting industry etc. In this paper, a new two-step method for the preparation of WC-Co cemented carbides was proposed. First, the mixture of yellow tungsten trioxide (WO3) and cobaltic oxide (Co2O3) were reduced by carbon black to remove all the oxygen. Then, the carbothermic reduction products were precisely mixed with an appropriate amount of carbon black to directly prepare WC-Co cemented carbides. The effects of C/WO3 ratio on the phase composition, morphological evolution, particle size and mechanical properties of products are investigated. The experimental results revealed that when the C/WO3 molar ratio was above 2.7, all oxygen in the raw material mixture were removed by carbon black and a mixture of W2C and η-phase were obtained after the first step of carbothermic reduction at 1150 °C for 2 h; then, the mixture of carbothermic reduction product and an appropriate content of carbon black was compacted, and the green compact was first carbonized at 1200 °C for 2 h and then sintered at 1450 °C for 4 h to prepare cemented carbides. With the increase of C/WO3 ratio at the first stage, the content of η-phase with a low melting point increased, which resulted in the large grain size of WC in the finally prepared cemented carbide. Compared with the traditional method of preparing cemented carbides, the cemented carbides prepared by the current method showed a higher hardness and toughness. Furthermore, the addition of a proper content of the VC in the second stage can significantly inhibit the grain growth of WC and further increase the hardness of cemented carbides.

Synthesis Of Ultrafine Wc-Co Composite Powders Under Hydrogen Atmosphere With Insitu Carbon Via A One-Step Reduction-Carbonization Process

Investigation of Carbon Source and Atmosphere During Reduction–Carbonization Process of Synthesizing WC–Co Composite Powders Via Spray Conversion Method

Synthesis of WC-0.67wt.%Cr3C2 nanopowders by a one-step reduction-carbonization method and their characterization

Rapid synthesis of ultrafine WC-Co cemented carbides by in-situ reactions and spark plasma sintering

Preparation of Nanoscale WC Powders by Sol-Gel Synthesis and Carbon Monoxide Carbonization

Preparation of nano-scaled WC powder by low-temperature carbothermic reduction method

A Novel Method for Direct Synthesis of WC-Co Nanocomposite Powder

WC-VC/Cr3C2 composite powders prepared by a carbothermic reduction-carburization process

WC Strengthened W–Cu Nanocomposite Powder Synthesized by In-Situ Reactions

Effect of Co on morphology and preparation of in situ synthesis of WC-Co composite powders

Microhomogeneous WC-TiC-Co composite powders with enhanced sinterability via a two-step carburization method

A short and facile process to synthesize WC-Co cemented carbides

Preparation and characterization of W@WCx composite powder by oxidation-vacuum carbonization process

Ultrafine and Nanoscaled Tungsten Carbide Synthesis from Colloidal Carbon Coated Nano Tungsten Precursor

Synthesis and Characterizations of Nanocrystalline Wc-Co Composite Powders by A Unique Ball Milling Process

Synthesis and Characterization of WC—VC—Co Nanocomposite Powders Through Thermal-Processing of a Core—shell Precursor

Preparation of Wcu Composite Powders by Sol-Gel Method and Their Reduction Behavior

Low-temperature Rapid Synthesis of Ultrafine Hafnium Carbide Ceramic Powders

In-situ synthesis of core-shell structure W(WC) composite grains in W-Cu composites fabricated by infiltration

Preparation and characterization of high-performance in-situ synthesized WC reinforced nickel-based coatings

Study on the preparation mechanism of novel WC-Cr2(C, N)-Co nanocomposites