Abstract:In this paper, several 60 mm diameter CdZnTe crystal ingots, containing large-size single crystals, were grown using (111) or (211) orientation seeds by the modified vertical Bridgman method. The Zn concentration distribution along the axial direction of the ingots was measured by near-infrared transmission spectroscopy at room temperature. The partition coefficient of Zn during the growth was calculated to be about 1.2. Zinc distribution uniformity measurements were carried out using photoluminescence mapping measurement at 80 K, which showed that the band gap variation in the CdZnTe wafers is less than 0.004 eV. IR microscopy showed that the diameters of the Te inclusions present in the material are in the range 6-9 mum, and the density of the inclusions is 1~3times105 cm-3. IR transmission measurements in the wave number region from 500 to 4000 cm-1 demonstrate that the IR transmittance of CdZnTe wafers is higher than 60%. Current-voltage measurements were performed on test structures fabricated using thermally evaporated Au contacts deposited on as-grown crystals, which revealed bulk resistivity values of 2~5times1010 Omegamiddotcm. Typical leakage currents for the planar devices were ~ 4 nA at a field strength of 1500 Vcm-1. The electron and hole mobility-lifetime products were evaluated using alpha particle irradiation. The obtained typical (mutau)e and (mutau)h values for the as-grown CdZnTe were 2.3times10-3 cm2V-1 and 1.5times10-4 cm2V-1, respectively.

Comparison of ZnTe Bulk Crystals Grown by the Temperature Gradient Solvent Method Using Elemental and Compound Materials

Improvement of the Thz Response of Zn1-Xmnxte Bulk Crystals Grown by A Temperature Gradient Solution Method

Growth and Characterization of Cdznte Bulk Crystals Grown by Temperature Gradient Solution Growth

Growth of Large-Size High-Quality ZnTe Bulk Crystals by Traveling Solvent Melting Zone Method

The Synthesis of Large-Diameter Znte Crystal for Thz Emitting and Detection

Growth and characterization of ZnTe single crystal via a novel Te flux vertical Bridgman method

Growth of ZnTe Semiconductor Crystal Via a Te Flux Zone Melting Method and Characterization of Its Properties

Growth of ZnTe single crystals from Te solution by vertical Bridgman method with ACRT

Characterization of Cr-Doped Znte Crystals Grown by Temperature Gradient Solution Growth (Tgsg)

Optical and Electrical Properties of Vanadium-Doped ZnTe Crystals Grown by the Temperature Gradient Solution Method

Characterization and Chemical Surface Texturization of Bulk ZnTe Crystals Grown by Temperature Gradient Solution Growth

The Transport Phenomena During the Growth of ZnTe Crystal by the Temperature Gradient Solution Growth Technique

Characterization of CdZnTe Crystals Grown Using a Seeded Modified Vertical Bridgman Method

Growth of Cd1−xZnxTe Crystals with Different X Values and Their Qualities Comparison

Study of Zn1−xQxTe(Q=Mn, V) Crystals Grown from Te-Rich Solution As Terahertz Emitters and Sensors

Tailoring structure imperfection in ZnTe bulk crystals and improving the terahertz response

Growth of ZnTe crystal via directional solidification method and study of its mechanical properties

Research into the Electrical Property Variation of Undoped CdTe and ZnTe Crystals Grown under Te-rich Conditions

Molecular Beam Epitaxy and Characterizations of PbTe Grown on GaAs(211) Substrates Using CdTe/ZnTe Buffers

Zn1-xMgxTe and P:Zn1-xMgxTe (X=0.06-0.25) Bulk Crystals Grown by Travelling Te Solution Method

Growth and Characterization of <110> Oriented ZnTe Single Crystal