Improvement of the Thz Response of Zn1-Xmnxte Bulk Crystals Grown by A Temperature Gradient Solution Method

Yadong Xu,Jiangpeng Dong,Hongjian Zheng,Bao Xiao,Leilei Ji,Yihui He,Caihong Zhang,Binbin Zhang,Wanqi Jie
DOI: https://doi.org/10.1039/c7ce00463j
IF: 3.756
2017-01-01
CrystEngComm
Abstract:As a type of A(1-x)(II)Mn(x)B(VI) alloy, Zn1-xMnxTe ingots with a diameter of 30 mm are grown as large single crystals by a temperature gradient solvent method under Te-rich conditions. The orange-red Zn1-xMnxTe crystals are cut and processed into size-appropriate wafers for fundamental studies, as well as for THz spectroscopy and magnetization response analyses. Mn segregation associated with the growth conditions is identified in the as-grown crystals, and an enriched higher concentration of Mn is observed inside the Te inclusion. To evaluate the effect of Mn on the Zn1-xMnxTe crystal, the site occupation is calculated via an ab initio study, and is further confirmed by electrical and optical property measurements. Mn tends to substitute Zn to form Mn-Zn in Zn1-xMnxTe, which results in a low density of free charge carriers, through which the THz detection sensitivity is enhanced by 1525% compared to the intrinsic ZnTe. Moreover, evident paramagnetic magnetization behavior is observed at variable temperatures due to the random distribution of an isolated Mn (Mn-ioct,Mn-Te6) spin with S = 5/2. We note that further optimization of the THz performance can be achieved by optimizing the growth process and tailoring the Mn content.
What problem does this paper attempt to address?