Abstract:In this work, the WC-Cr2(C, N)-Co nanocomposites were synthesized by using the one-pot carbothermal reduction nitridation hydrothermal precursor method. The preparation mechanisms, including phase and morphology evolutions, were investigated by differential thermal analysis (TG-DSC), X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray photoelectron spectroscopy (XPS), and thermodynamic analysis. The results showed that phase evolution, with temperature increasing, follows the sequences of (amorphous phase, WO2.72) → (CoWO4, WO2.72, WO2, CrWO3) → (WO2, CoWO4, Co6W6C, CrWO3) → (W2C, Co3W3C, WC) → (WC, W2C, Co3W3C) → (WC, Co, Co3W3C trace amount). Through comparing different heat treatment conditions, the powder particle size was more easily affected by temperature than holding time. The higher temperatures or longer time holding resulted in the aggregation of powder particles. Finally, WC-Cr2(C, N)-Co nanopowders with about 60 nm were obtained at 1050 °C for 1 h under the N2 flow of 1 L/min with the oxygen content of 0.22 wt% and the free carbon content of 0.19 wt%. The TEM elements mapping revealed that Cr distributes uniformly with WC grains, Co and WC grains are combined well. The surface of WC-Cr2(C, N)-Co determined by XPS is mainly composed of W, Co, Cr, C, N, and O. The spark plasma sintering (SPS) sintered WC-Cr2(C, N)-Co composite shows a nanocrystalline microstructure with the average grain size ∼170 nm, and the excellent comprehensive mechanical properties with the Vickers hardness 1730 Kg·mm−2 and fracture toughness 11.5 MPa·m1/2, respectively.

Synthesis of ultrafine WC-10Co composite powders with carbon boat added and densification by sinter-HIP

Influences of Ni/Cu/Cr3C2 Composite Additive on Microstructure and Properties of WC–10Co Fine Grained Hardmetal

Synthesis Of Ultrafine Wc-Co Composite Powders Under Hydrogen Atmosphere With Insitu Carbon Via A One-Step Reduction-Carbonization Process

Microhomogeneous WC-TiC-Co composite powders with enhanced sinterability via a two-step carburization method

A Novel Method for Direct Synthesis of WC-Co Nanocomposite Powder

In-situ synthesis of core-shell structure W(WC) composite grains in W-Cu composites fabricated by infiltration

Rapid synthesis of ultrafine WC-Co cemented carbides by in-situ reactions and spark plasma sintering

Microstructure Evolution and Hardness Improvement of WC-Co Composites Sintered with Fe Substituting Part of Co Binder

Synthesis of Y2O3-doped WC-Co powders by wet chemical method and its effect on the properties of WC-Co cemented carbide alloy

Preparation of low binder WC-Co-Ni cemented carbides with fine WC grains and homogeneous distribution of Co/Ni

Microstructures and Properties of WC-10 wt.%CoCrFeNiAlx Composite Cemented Carbides

Carbon control and densification of WC-8%Co fabricated by extrusion-based additive manufacturing under pressureless sintering

Synthesis and Characterizations of Nanocrystalline Wc-Co Composite Powders by A Unique Ball Milling Process

Synthesis of WC-0.67wt.%Cr3C2 nanopowders by a one-step reduction-carbonization method and their characterization

Study on the preparation mechanism of novel WC-Cr2(C, N)-Co nanocomposites

Microstructural characteristics, mechanical properties and interfacial formation mechanism of tungsten alloy/steel composite structure fabricated by HIP co-sintering

Preparation and characterization of W@WCx composite powder by oxidation-vacuum carbonization process

Characterizations of Ball-Milled Nanocrystalline WC–Co Composite Powders and Subsequently Rapid Hot Pressing Sintered Cermets

WC-VC/Cr3C2 composite powders prepared by a carbothermic reduction-carburization process

Enhancement of the mechanical properties of ultrafine-grained WC-Co cemented carbides via the in-situ generation of VC

Preparation and characterization of high-performance in-situ synthesized WC reinforced nickel-based coatings