Abstract:Two compositions Ce0.50Zr0.39La0.04Y0.07O2−δ and Ce0.25Zr0.65La0.04Y0.06O2−δ based on ceria-zirconia solid solutions were prepared as nanopowders using a continuous hydrothermal flow synthesis reactor, followed by either freeze-drying or hotplate-drying of the slurry. Each dried nanopowder was then subjected to 10h heat-treatment at 1000°C, 1100°C or 1200°C in air (to simulate accelerated ageing). The reducibility and hydrogen consumption of the oxidised samples were measured using temperature programmed reduction (TPR) up to 1000°C. The effects of composition, drying method and heat-treatment temperature were evaluated on the TPR profiles of the materials. The powders were further investigated using a range of analytical methods including UV/Vis spectroscopy (which yielded colour data), Raman spectroscopy, powder X-ray diffraction, BET surface area measurements and X-ray photoelectron spectroscopy (XPS). Chemometric methods were used to investigate relationships between the spectroscopic and total oxygen storage capacity (OSC) data. Principal component analysis (PCA) was used to provide a simple interpretation of the effects of various synthesis and treatment parameters on Raman spectra. Principal component regression (PCR) was used to build regression models relating the Raman spectra and the temperature of hydrogen consumption peak at several set temperatures in the TPR. The total hydrogen consumption of the materials was generally high, while the drying and heat-treatment conditions appeared to have a significant effect on the final properties of the resulting powders, such as the surface area and total oxygen storage capacity.

Heat Treatment During Preparation of Nano-zirconia Powders by the Liquid-phase Process

Preparation of Zirconia Powders by Sol-gel Process

Effects of Heat-Treatment Temperature on Preparation of the Sol-Gel-Derived Ag/TiO2 Films

Synthesis and Characterization of Doped Nano-Sized Ceria–zirconia Solid Solutions

Preparation and Microstructure of Nanometer Tetragonal Polycrystal Zirconia Powder at Low Temperature Condition

Effect of Heat-treatment Atmosphere on Preparation of Continuous Zirconia Fibers

Preparation of Nano-ZrO2 powder via a microwave-assisted hydrothermal method

Effects of Precipitators and Surfactants on the Preparation of Zirconia Nanopowders via Solvothermal Method

Preparation and Luminescence of ZrO_2 Nanopowders Via Solvothermal Method

Hydrothermal Synthesis and Characterization of Zirconia Nanocrystallites

Co-precipitation of nano Mg–Y/ZrO2 ternary oxide eutectic system: Effects of calcination temperature

Research of ZrO2 Nano Powders Sintering Properties

Study on the process and properties of nano-sized polycrystal zirconia powders by co-precipitation in super-alkaline medium

Preparation of spherical zirconia powder by nano-reactor of microemulsion and its densification behavior

Effect of Heat Treatment on the Properties of Nano-Diamond under Oxygen and Argon Ambient

Preparation and Self-assembly of Zirconia Nanoparticles Via Hydrothermal Method

The Process and Properties of Nanometer Zirconia Powder by Environmental Benign Method

PREPARATION AND PROPERTIES OF NANOMETER POLYCRYSTALS ZIRCONIA POWDER BYSUPER ALKALINE METHOD AT LOW TEMPERATURE WITH ORGANIC ADDITIVES

Preparation of Zirconia Base Solid Solution Nanopowder by Exothermal Solid-State Synthesis

OPTIMIZATION OF HEAT TREATMENT TECHNOLOGY OF NANO Al2O3 POWDERS

Study on a new, environmentally benign method and its feasibility of preparing nanometer zirconia powder