Abstract:Indium tin oxide (ITO) thin films were deposited on glass substrates by ion beam sputter deposition method in three different deposition conditions [(i) oxygen (O2) flow rate varied from 0.05 to 0.20sccm at a fixed argon (1.65sccm) flow rate, (ii) Ar flow rate changed from 1.00 to 1.65sccm at a fixed O2 (0.05sccm) flow rate, and (iii) the variable parameter was the deposition time at fixed Ar (1.65sccm) and O2 (0.05sccm) flow rates]. (i) The X-ray diffraction (XRD) patterns show that the ITO films have a preferred orientation along (400) plane; the orientation of ITO film changes from (400) to (222) direction as the O2 flow rate is increased from 0.05 to 0.20sccm. The optical transmittance in the visible region increases with increasing O2 flow rate. The sheet resistance (Rs) of ITO films also increases with increasing O2 flow rate; it is attributed to the decrease of oxygen vacancies in the ITO film. (ii) The XRD patterns show that the ITO film has a strong preferred orientation along (222) direction. The optical transmittance in the visible spectral region increases with an increase in Ar flow rate. The Rs of ITO films increases with increasing Ar flow rate; it is attributed to the decrease of grain size in the films. (iii) A change in the preferred orientations of ITO films from (400) to (222) was observed with increasing film thickness from 314 to 661nm. The optical transmittance in the visible spectral region increases after annealing at 200°C. The Rs of ITO film decreases with the increase of film thickness.

Preparation of Nano-sized Powder of Indium Tin Oxide (ITO)

P-type Tin–indium Oxide Films Prepared by Thermal Oxidation of Metallic InSn Alloy Films

P-type Transparent Conducting Indium-Tin Oxide Thin Films Deposited by Spray-pyrolysis

Sol–gel Synthesis and Sintering of Nano-Size Li2TiO3 Powder

The Characterization and Preparation of Nano Scale Fe Doping TiO2 by Sol Gel Method? the Crystallization and Thermal Decomposition Process of Fe Doping TiO2 Xerogel Powders Using Thermal TG IR Spectrometry

Optimization Preparation of Indium Tin Oxide Nanoparticles via Microemulsion Method Using Orthogonal Experiment

The Thermal Analysis, Crystal Growth And Structure Transformation Of Nano-Scale Tio2 Prepared By Ticl4 Hydrolysis

Preparation and characterization of hollow spherical indium tin oxide with micro size by template assisted hydrothermal method

Preparation of extraordinary high-density indium-tin oxide target on the basis of pressure-less sintering method

A Size-Controllable Preparation Method for Indium Tin Oxide Particles Using A Membrane Dispersion Micromixer

Optimization Hydrothermal Synthesis Conditions for Nano-Sized (na0.5 Bi0.495 Nd0.005 )tio3 Particles by an Orthogonal Experiment and Their Luminescence Performance.

Hydrothermal Preparation and Characterization of Nanocrystalline Porous Tin Dioxide Thin Films

Preparation and Performance of Nano-ITO/WPU Organic-Inorganic Hybrid Heat Insulation Materials

TiO2 THIN FILMS PREPARED BY SPIN COATING TECHNIQUE

Preparation and Electrical Properties of Electrospun Tin-Doped Indium Oxide Nanowires

Preparation And Characterization Of Nano-Yb2o3/Tio2 Particles

PREPARATION OF IRON-DOPED TITANIA NANOCRYSTALLINE GRAINS AND ITS PHOTOCATALYTIC PROPERTY

Hydrothermal Preparation and Characterization of Nanocrystalline Powder of β-Indium Sulfide

Preparation and Characterization of Nano-Tio2 Powder

Characterization of nanocrystalline indium tin oxide thin films prepared by ion beam sputter deposition method

Molecular Mechanism of Monodisperse Colloidal Tin-Doped Indium Oxide Nanocrystals by a Hot-Injection Approach.