Optimization Hydrothermal Synthesis Conditions for Nano-Sized (na0.5 Bi0.495 Nd0.005 )tio3 Particles by an Orthogonal Experiment and Their Luminescence Performance.
Xiyue He,Wenxiang Li,Bijun Fang,Shuai Zhang,Xiaolong Lu,Jianning Ding
DOI: https://doi.org/10.1002/bio.4018
IF: 2.613
2021-01-01
Luminescence
Abstract:By designing an orthogonal experiment with four factors and three levels, (Na0.5Bi0.495Nd0.005)TiO3 (NBT-Nd) nanopowders were prepared using a hydrothermal method under different conditions to determine the optimum hydrothermal synthesis conditions. The synthesized NBT-Nd nanopowders were characterized using X-ray diffraction measurement, ultraviolet-visible spectra, photoluminescence spectra, and transmission electron microscopy to evaluate the orthogonal experimental conditions. The results showed that NBT-Nd powders with excellent crystalline and luminescence properties could be obtained at 160 degrees C, with a 16 h reaction time, 8 mol center dot L-1 NaOH, and with 0.4489 g C19H42BrN. The optimized hydrothermal method-prepared NBT-Nd powder has a rather pure rhombohedral perovskite structure at room temperature, and exhibits an aggregated polycrystalline structure containing nanotubes and nano-sized particles. Under excitation of 247 nm light, strong fluorescence emissions are excited at 423 nm and 441 nm in the NBT-Nd powder that were generated by transitions of Nd3+ from D-2(5/2) to I-4(9/2) and from (4)G(11/2) to I-4(9/2), respectively. Through CIE1931 chromaticity calculation of the emission peaks, the NBT-Nd powder was shown to emit indigo blue fluorescent light.