Abstract:ZTM ceramics comprising of 0.75ZnAl(2)O(4)-0.25TiO(2) and MgTiO3 at a ratio of 90:10 wt.% are widely used in the field of communication as filters and resonators owing to their excellent microwave dielectric properties. However, the development of such dielectrics with complex structures, as required by microwave devices, is difficult using traditional fabrication methods. In this study, ZTM microwave dielectric ceramics were prepared using the digital light processing (DLP) technology. The influence of the sintering temperature on the phase composition, microstructure, and microwave dielectric properties of ZTM ceramics was investigated. Results showed that with an increase in the sintering temperature, the dielectric constant (epsilon(r)) and quality factor (Q x f) of ZTM ceramics initially increased owing to the increase in the density and diffusion of ions. However, when the sintering temperature was excessively high, the abnormal growth of crystal grains and micropores led to a decrease in epsilon(r) and Q x f. The ZTM ceramics sintered at 1450 degrees C exhibited the optimum microwave dielectric properties (epsilon(r) = 12.99, Q x f = 69 245 GHz, tau(f) = -9.50 ppm/degrees C) owing to the uniform microstructure and a high relative density of 95.02%. These results indicate that DLP is a promising method for preparing high-performance microwave dielectric ceramics with complex structures.

Study on Structural and Dielectric Properties of Ultra-Low-Fire Integratable Dielectric Film for High-Frequency and Microwave Application

A new low-loss microwave dielectric ceramic for low temperature cofired ceramic applications

Synthesis and characterization of phase pure and Mg-modified AgZnVO 4 microwave dielectrics for high-frequency ULTCC applications

A low loss low-temperature sintered ferrite-dielectric composite thick film for high-frequency application

Temperature stable microwave dielectric ceramic 0.3Li2TiO3–0.7Li(Zn0.5Ti1.5)O4 with ultra-low dielectric loss

Low-temperature Sintering and Microwave Dielectric Properties of ZnTiO3-based LTCC Materials

Investigation of PTFE-based ultra-low dielectric constant composite substrates with hollow silica ceramics

Microwave Dielectric Properties of (0.75znal2o4–0.25tio2)–mgtio3 Ceramics Prepared Using Digital Light Processing Technology

Surface-modified Zn0.5Ti0.5NbO4 particles filled polytetrafluoroethylene composite with extremely low dielectric loss and stable temperature dependence

ZrO2-doped Zn0.5Ti0.5TaO4 Microwave Dielectric Ceramics with Low Dielectric Loss and Excellent Temperature Stability

Structure and Properties of Low Temperature Sintered Znta2o6 Microwave Dielectric Ceramics

Research Progress of Ultra-Low Temperature Cofired Ceramics for Microwave Applications

Microwave dielectric properties of novel Na2Mg5-xZnx(MoO4)6 (x = 0–0.09) ceramics for ULTCC applications

Low-fired microwave dielectrics in ZnO-TiO 2 ceramics doped with CuO and B 2 O 3

Microwave dielectric properties of (0.75ZnAl 2 O 4 –0.25TiO 2 )–MgTiO 3 ceramics prepared using digital light processing technology

Study of the electromagnetic properties of the low-temperature sintering ferrite/ceramic composite materials

The Study of Dielectric Properties of ZnO-TiO2 Microwave Ceramic Sinterd at Low-temperature and Chip Multilayer Bandpass Filter

Research Progress of Low Temperatue Co-fired Microwave Dielectric Ceramics

MgTiO3/TiO2/MgTiO3: an Ultrahigh-Q and Temperature-Stable Microwave Dielectric Ceramic Through Cofired Trilayer Architecture

Microwave dielectric properties of LiZn4V3O12 composite ceramics sintered at low temperature and its LTCC application

A novel ultra-high Q microwave dielectric ceramic ZnMgTiO4 with spinel structure