Abstract:The defect-induced laser damage on mechanically machined fused silica optical surfaces under intense laser irradiation severely threatens the laser damage resistance of optical components. The lack of a quantitative relationship between the feature information of surface defects and the laser-induced damage thresholds (LIDTs) of optical surfaces poses a challenge to effectively evaluate the influence of the surface defects on the LIDTs of optical surfaces. Herein, the photoluminescence (PL) properties of the areas where laser damage tends to occur in surface-defect zones are explored. The PL induced by the point defects at the atomic scale in these areas is found to be obviously higher than that of other positions. The PL envelope area (S) at the position with the highest PL intensity among the whole surface defect is found to be inversely proportional to the LIDT (Φ) of the optical surface for the first time (SΦ = N0). It is beneficial to quantitatively characterize the influence of the surface defect and provide new insights in elucidating the defect-induced laser damage mechanisms. Besides, we found that there is a minimum LIDT for the mechanically machined optical surfaces with various surface defects. On basis of this, the maximum influence of the surface defects with different species on the LIDTs of optical surfaces could be determined. Based on the constructed relationship (SΦ = N0) and the developed MD model, two causes of the minimum LIDT are determined. The PL envelope area of the surface defect would slightly affect the LIDT when the PL envelope area is large enough, which is the first cause. The mechanical force could compact the optical surface, increasing the densities of Si and O atoms. However, the densities of Si and O atoms become stable when the mechanical force is large enough, causing the highest densities of point defects, which is the second cause.

Surface Molecular Structure Defects and Laser-Induced Damage Threshold of Fused Silica During a Manufacturing Process

Traceless Mitigation of Laser Damage Precursors on a Fused Silica Surface by Combining Reactive Ion Beam Etching with Dynamic Chemical Etching

Laser Induced Damage Characteristics of Fused Silica Optics Treated by Wet Chemical Processes

Correlation Between Photoluminescence Properties of Surface Defects and Laser-Induced Damage Threshold of Fused Silica

Characterization of artificial indentation defects in fused silica surface and its damage performance under 355 nm nanosecond laser

Interstitial O2 and Si-H Defects Produced in Fused Silica During Laser-Induced Damage

Laser Induced Damage in Fused Silica for 248 nm

The decisive effects of the stress states and brittle-plasticity of the surface defects on their laser-induced damage thresholds on fused silica surfaces

Ab Initio Molecular Dynamics Simulation of the Effect of Impurities on Laser-Induced Damage of Fused Silica

Evolution of Intrinsic Defects and Ring Structures on the Surface of Fused Silica Optics after CO2 Laser Conditioning.

The Infrared Spectra and Laser Damage Threshold of the Fused Silica after Megacoustic Field Assisted Hydrofluoric-Based Etching

The Influence of Etching Depth on Surface Molecular Structures and Laser Damage Thresholds of Fused Silica by using Megasonic-assisted HF-based Etching

Improving Uv Laser Damage Threshold Of Fused Silica Optics By Wet Chemical Etching Technique

Damage Growth Characteristics on the Exit Surface of Fused Silica by the Low-Temporal Coherence Light Irradiation.

Evolution of Point Defects in Mechanical Cracks of Fused Silica after CO2 Laser Melting

Relationship Between the Photoluminescence Envelope Area of Surface Defects and the Laser-Induced Damage Thresholds of Mechanically Machined Fused Silica Optical Surfaces

The Photo-Thermal Absorbing Influence on Introducing Laser-Damaging of the Fused Silica

Subsurface Damage on Ground Fused Silica Surfaces

Detailed Near-Surface Nanoscale Damage Precursor Measurement and Characterization of Fused Silica Optics Assisted by Ion Beam Etching

Investigation on the influence of the CO2 laser parameters on the defect healing process of fused silica

Structural Defects in Ultra-Low Laser Absorption Fused Silica