Abstract:Although no optically visible damage is produced in the fused silica under laser irradiation below its laser-induced damage threshold (LIDT), defect proliferation may occur due to the evolution of its internal atomic structure. The escalation in defect content leads to heightened absorption, and resulting in the degradation of the optical performance of the optics. In recent decades, there have been a lot of experimental studies on laser-induced damage and laser conditioning, but there is still a great lack of in-depth understanding and theoretical analysis of the evolution process of point defects in fused silica. In this study, the emphasis is on the evolution of point defects and fatigue damage in fused silica under multi-pulse nanosecond laser irradiation. To address this, a point-defect evolution model is developed, and the coupled evolution law of temperature and defect during laser irradiation is derived by integrating it with a numerical model. The results demonstrate that the model effectively predicts the defect evolution of fused silica under laser irradiation and facilitates the prediction of fatigue damage. It is revealed that the rate of defect evolution in fused silica is more influenced by temperature than stress, and a temperature threshold can be used to judge the condition of damage occurrence. Furthermore, through an analysis of the effect of laser fluence on defect relaxation rate, a defect relaxation method employing variable laser fluence was proposed. This study provides a reliable theoretical analysis method for understanding the fatigue damage induced by multi-pulse laser irradiation in fused silica and offers a new perspective for the annealing treatment of point defects in fused silica. (c) 2024 Optica Publishing Group under the terms of the Optica Open Access Publishing Agreement

Evolution of Intrinsic Defects and Ring Structures on the Surface of Fused Silica Optics after CO2 Laser Conditioning.

Evolution of Point Defects in Mechanical Cracks of Fused Silica after CO2 Laser Melting

Investigation on the influence of the CO2 laser parameters on the defect healing process of fused silica

Analysis Method of Point Defects Evolution in Fused Silica under Multi-Pulse Nanosecond Laser Irradiation

Correlation Between Photoluminescence Properties of Surface Defects and Laser-Induced Damage Threshold of Fused Silica

Material migration and damage characteristics of fused silica optical surface treated by CO 2 laser/short – pulse ultraviolet laser

Surface Molecular Structure Defects and Laser-Induced Damage Threshold of Fused Silica During a Manufacturing Process

Damage Growth Characteristics on the Exit Surface of Fused Silica by the Low-Temporal Coherence Light Irradiation.

The Structure Evolution of Fused Silica Induced by CO 2 Laser Irradiation

The Influence of Co2 Laser Local Irradiation on the Laser Damage Resistance of Fused Silica

Morphology evolution mechanisms and localized structural modification of repaired sites on fused silica optics processed by CO2 laser rapid ablation mitigation

Formation Mechanism of Bubbles in the Crack Healing Process of Fused Silica Using a CO2 Laser

Surface Evolution and Laser Damage Resistance of CO2 Laser Irradiated Area of Fused Silica

Research on Laser-Induced Damage Post-Restoration Morphology of Fused Silica and Optimization of Patterned CO2 Laser Repair Strategy

Characterization of artificial indentation defects in fused silica surface and its damage performance under 355 nm nanosecond laser

Surface Defects, Stress Evolution, and Laser Damage Enhancement Mechanism of Fused Silica under Oxygen-Enriched Condition

Development of Damage Growth Mitigation in Fused Silica by CO2 Laser

Evolution of point defects in mechanical cracks of fused silica after CO_2 laser melting

Formation Mechanism of Surface Morphology in the Process of CO2 Pulsed Laser Processing of Fused Silica Optics

New Progress of CO2 Laser Processing Techniquesfor Fused Silica Optics

Combined Studies of Surface Evolution and Crack Healing for the Suppression of Negative Factors During CO2 Laser Repairing of Fused Silica