Abstract:Localized CO2 laser repairing of surface damage on fused silica optics has been successfully applied in high-power laser system in the field of controllable nuclear fusion. In order to accurately predict the surface topography evolution and to reveal the intrinsic physical mechanism during the process of laser mitigation, experiments of localized CO2 laser mitigation were firstly carried out to analyze the features of mitigated craters under different laser powers. Then a multi-physics coupled mathematical model was developed based on the fluid control equation, heat and mass transfer equation and material phase transition kinetics to investigate the thermodynamic and kinetic behaviors of laser interaction with silica. The model considered the effects of Marangoni convection, gravity, capillary force and vaporization recoil pressure, as well as the nonlinear variation of physical parameters of silica material with respect to temperature. The results showed that with the increase of laser power, the material ablation and the appearance of raised rim occurred simultaneously. The depth of the mitigated crater increased sharply when the threshold for material ablation was attained, while the lateral dimension increased linearly. The vaporization recoil pressure was found to be the dominant factor for the formation of Gaussian crater with the raised rim feature. The capillary force caused the material at the edge of the molten pool to have a tendency to reflow after laser shutting down, but it was too small to change the surface topography. This work could significantly contribute to the understanding of laser mitigation process, which laid the foundation for the accurate prediction and evaluation of surface quality of CO2 laser repaired fused silica surface.

Material migration and damage characteristics of fused silica optical surface treated by CO 2 laser/short – pulse ultraviolet laser

Research on Laser-Induced Damage Post-Restoration Morphology of Fused Silica and Optimization of Patterned CO2 Laser Repair Strategy

Research Development of CO2 Laser Treatment for Repair Damage in Fused Silica

Morphology evolution mechanisms and localized structural modification of repaired sites on fused silica optics processed by CO2 laser rapid ablation mitigation

Investigation on the influence of the CO2 laser parameters on the defect healing process of fused silica

Experimental and Theoretical Investigation of Localized CO2 Laser Interaction with Fused Silica During the Process of Surface Damage Mitigation

Effects of CO2 Laser Irradiation on Surface Morphology and Stress Distribution of Fused Silica

Repaired Morphology Induced Optical Modulation in Fused Silica Based on Scalar Diffraction Theory

Surface Evolution and Laser Damage Resistance of CO2 Laser Irradiated Area of Fused Silica

New Progress of CO2 Laser Processing Techniquesfor Fused Silica Optics

Incident Laser Modulation of a Repaired Damage Site with a Rim in Fused Silica Rear Subsurface

Localized Co2 Laser Treatment and Post-Heating Process to Reduce the Growth Coefficient of Fused Silica Surface Damage

Surface Damage Mitigation of Fused Silica with CO2 Laser

Repair of Fused Silica Damage Using Selective Femtosecond Laser-Induced Etching

Correlation Between Photoluminescence Properties of Surface Defects and Laser-Induced Damage Threshold of Fused Silica

Coupled Thermal-Mechanical Analysis of CO<sub>2</sub> Laser Irradiation on Fused Silica

Microsecond-pulsed CO2 laser cleaning of high damage threshold fused silica

Combined Studies of Surface Evolution and Crack Healing for the Suppression of Negative Factors During CO2 Laser Repairing of Fused Silica

Theoretical and Experimental Investigations of Localized CO2 Laser-Fused Silica Interactions and Thermo-Mechanical Properties of Mitigated Sites

Development of Damage Growth Mitigation in Fused Silica by CO2 Laser

Rapid and Non-Destructive Repair of Fused Silica with Cluster Damage by Magnetorheological Removing Method