Abstract:Achieving an optimal balance between mechanical properties, dielectric properties, and thermal shock resistance presents a significant challenge in the development of advanced ceramics. This study investigates Si3N4-BN composite materials, prepared by hot-press sintering with magnesium aluminum silicate (MAS) as the sintering additive, to assess the impact of varying hexagonal boron nitride (h-BN) content on their mechanical and dielectric properties, as well as their thermal shock resistance. At an h-BN content of 20 wt.%, the BN layers act as a toughening phase through a pull-out mechanism, minimally impacting the composite's density. This composition results in superior fracture toughness (7.4 MPa·m1/2), high strength (598 MPa), low dielectric constants (∼6.8), and dielectric loss (∼7.4×10-3). Notably, after a thermal shock at 1000°C, the composite exhibits a peak residual strength of 621 MPa, surpassing its initial strength. This enhanced performance is attributed to the formation of a dense Mg-Al-Si-B-O oxide glass layer on the surface during thermal shock, which not only repairs surface defects but also induces compressive stress. The development of the Si3N4-BN-MAS composite, with its outstanding comprehensive performance, marks a significant advancement for materials used in high-temperature wave transmission applications.

Thermal Shock Resistance of Si3N4/h-BN Composites Prepared Via Catalytic Reaction-Bonding Route

Enhanced thermal shock resistance of BN-based composites sintered by hot-pressing with the introduction of nano oxides

Effect of Boron Nitride Content on Mechanical、dielectric and Thermal Shock Resistance Properties of Si3N4-BN-MAS Composites

Cyclic thermal shock resistance of h-BN composite ceramics with La2O3–Al2O3–SiO2 addition

Thermal Shock Resistance of Nano BN-SiC Composites

Cyclic thermal shock resistance of h-BN composite ceramics with La<sub>2</sub>O<sub>3</sub>-Al<sub>2</sub>O<sub>3</sub>-SiO<sub>2</sub> addition

Microstructure, mechanical properties and thermal shock behavior of h-BN-SiC ceramic composites prepared by spark plasma sintering

Thermal Shock Behavior of Si3N4/BN Fibrous Monolithic Ceramics

Thermal Shock Behavior of Si 3 N 4 /BN Fibrous Monolithic Ceramics.

Thermal shock resistance of in situ formed SiC–BN composites

Thermal properties and thermal shock resistance of BAS-BN composite ceramics

Thermal Shock Resistance of the Porous Boron Nitride/silicon Oxynitride Ceramic Composites

Effects of H-Bn on Mechanical Properties of Reaction Bonded Β-Sialon/h-bn Composites

Effects of h‐BN on the thermal shock and oxidation resistance of SiO2‐bonded SiC refractories

Effect of SiC Content on Mechanical Properties and Thermal Shock Resistance of BN–ZrO2–SiC Composites

Microstructure, mechanical properties and thermal shock behavior of h-BN–AlN ceramic composites prepared by combustion synthesis

Study on Thermal Shock Behavior of SiC/BN Laminated Ceramic Composites

Enhanced Strengths and Thermal Shock Resistance of SiC-BN-10 Vol% Cf Composites Through ZrB2 Addition

Single-cycle thermal shock resistance of ZrB2–SiCnp ceramic composites

High temperature thermo-physical properties and thermal shock behavior of metal–diborides-based composites