Role of Mo Addition on Structure and Magnetic Properties of the Fe85Si2B8P4Cu1 Nanocrystalline Alloy

Xingjie Jia,Yanhui Li,Guoqiang Xie,Tianlong Qi,Wei Zhang
DOI: https://doi.org/10.1016/j.jnoncrysol.2017.12.003
IF: 4.458
2018-01-01
Journal of Non-Crystalline Solids
Abstract:The amorphous-forming ability (AFA), crystallization structure and magnetic properties of the melt-spun Fe85−xSi2B8P4Cu1Mox (x=0–2) alloys were investigated. The addition of 1–2at% Mo in the Fe85Si2B8P4Cu1 alloy enhances the AFA with increasing the critical thickness for amorphous formation from ~14 to ~20μm. The Mo alloying refines the microstructure and reduces the coercivity of the annealed alloys, and weakens the dependence of the coercivity on the heating rate, although it decreases the saturation magnetic flux density. After annealing under a low heating rate of 50K/min, the average α-Fe grain size and coercivity of the Fe84Si2B8P4Cu1Mo1 alloy are ~25nm and 23.9A/m, respectively, which are lower than those of ~32nm and 40.5A/m for the base alloy. In addition, the mechanism related to the effects of Mo on the structure and magnetic properties was discussed in term of the crystallization activation energy.
What problem does this paper attempt to address?