On the glass forming ability (GFA), crystallization behavior and soft magnetic properties of nanomet-substituted alloys

E. Dastanpour,M.H. Enayati,A. Masood,V. Ström

DOI: https://doi.org/10.1016/j.jnoncrysol.2019.119774

2020-02-01

Abstract:This study was aimed to investigate the effect of substitution of Fe with Co, C, and Mo on the glass forming ability (GFA), crystallization behavior, and magnetic properties of Fe–B–Si–P–Cu (Nanomet) alloy. The thermodynamic parameters, PHS and PHSS, were used to guide towards increased GFA. The PHSS enhanced from −2.04 kJ/mol for Nanomet to −4.83 kJ/mol for a Co4C1Mo1 (at.%) substituted alloy. As a result, the critical quench rate reduced significantly, manifested as a drop of the required rotational speed from 3000 rpm to 2000 rpm. The temperature interval between two crystallization peaks enlarged for the substituted alloy, allowing a broader annealing range for nanocrystallization. The saturation magnetization (MS) and the coercivity (HC) were nearly maintained. This work confirms the relevance of the parameters PHS and PHSS to improve the GFA of the Nanomet alloy, and it is suggested that the same strategy can be applied for other alloys.

materials science, multidisciplinary, ceramics

What problem does this paper attempt to address?

This paper aims to study the effects of partially replacing Fe (iron) elements with Co (cobalt), C (carbon) and Mo (molybdenum) on the glass - forming ability (GFA), crystallization behavior and soft magnetic properties of Nanomet alloys. Specifically, the author hopes to improve the glass - forming ability of Nanomet alloys through this substitution while maintaining or only slightly losing their soft magnetic properties.

Thermodynamic parameters \(P_{HS}\) and \(P_{HS^*}\) are used in the paper to guide the improvement of the glass - forming ability of Nanomet alloys. These parameters consider the chemical mixing enthalpy, mismatch entropy and configurational entropy to systematically improve the glass - forming ability. It is found that when Fe is replaced by 4 at% Co, 1 at% C and 1 at% Mo, \(P_{HS^*}\) increases from \(- 2.04\) kJ/mol to \(-4.83\) kJ/mol, indicating that the glass - forming ability has been significantly improved.

In addition, the study also found that through this substitution, the critical quenching rate of Nanomet alloys is significantly reduced, which is manifested as the required rotation speed dropping from 3000 rpm to 2000 rpm. The crystallization temperature interval is also widened, making the annealing range in the nanocrystallization process wider. At the same time, the saturation magnetization \(M_S\) and coercivity \(H_C\) remain almost unchanged.

Overall, this work verifies the relevance of the \(P_{HS}\) and \(P_{HS^*}\) parameters in improving the glass - forming ability of Nanomet alloys and suggests that the same strategy can be applied to other alloy systems.