Abstract:In this study, IN-718 samples were printed using laser powder bed fusion (LPBF) process to investigate the effect of printing parameters (in terms of Volume Energy Density, (VED)), printing orientation, heat treatment and test temperature on the microstructure and mechanical properties. Tensile properties were evaluated using small-scale tensile specimens extracted from samples printed with 15 different processing parameters (by varying scan speed and scan power) in two print orientations (XY and XZ plane), in three microstructural conditions (as-printed (AP), printed + solution treated and aged (STA), printed + hot isostatically pressed (HIP) + STA), at two different temperatures (room temperature and 650 °C). The mechanical properties obtained from testing of small-scale tensile specimens were compared with results obtained from testing of specimens following ASTM E8 standard, to understand effect of specimen size on mechanical properties. Based on microstructural analysis, it was observed that below a VED value of 50 J/mm 3 , the conduction region prevailed, with the presence of irregular lack of fusion porosities. In VED range of 50–100 J/mm 3 , transition prevailed with highly dense samples (over 99 % of theoretical density) with minimal porosity. Above a VED of 100 J/mm 3 , keyhole regime prevailed with the presence of spherical keyhole porosities. STA heat treatment improved YS and UTS to ∼1200 and ∼1400 MPa, respectively, while reducing ductility to ∼15 %. HIP + STA had similar effect on tensile properties as STA heat treatment. Based on tensile strength data, it was observed that HIP is not essential for parts printed with optimum parameters. Sample size in the present study was found to have an insignificant effect on tensile properties. In conclusion, the study provides an insight into the role played by printing parameters, printing orientation, and post-processing on defects, microstructures and thereby on the mechanical properties.

Engineered microstructure evolution in inconel 718 via laser powder bed fusion through a novel element-based approach

The evolution of microstructure and mechanical properties of Inconel 625 alloy fabricated by laser powder bed fusion via novel hybrid scanning strategy

Microstructural, mechanical and wear behaviour of Inconel-718 produced through laser-powder bed-fused additive manufacturing

Novel strengthening mechanism of laser powder bed fusion-manufactured Inconel 718: Effects of customized hierarchical interfaces

Microstructure and mechanical property comparison of Inconel alloys fabricated using micro and conventional laser powder bed fusion

Mechanical Characterization of Near-Isotropic Inconel 718 Fabricated by Laser Powder-Bed Fusion

Microstructure and mechanical properties at elevated temperatures of as-built and heat-treated Inconel 718 produced through laser powder bed fusion processes

Inconel 718 produced by laser powder bed fusion: an overview of the influence of processing parameters on microstructural and mechanical properties

Unique crystallographic texture formation in Inconel 718 by laser powder bed fusion and its effect on mechanical anisotropy

The microstructural evolution and mechanical response of laser direct energy deposition Inconel 718 alloy based on simulation and experimental methods

ICME framework to simulate microstructure evolution during laser powder bed fusion of Haynes 282 nickel-based superalloy

High-throughput investigation of laser powder bed fabricated Inconel 718 alloy: Fabrication, microstructure and performance

Mechanical properties of laser powder bed fusion processed Inconel alloy IN718 in different heat treatment conditions through small scale specimen testing

Integrating Phase Field Modeling and Machine Learning to Develop Process-Microstructure Relationships in Laser Powder Bed Fusion of IN718

A review on microstructure, mechanical behavior and post processing of additively manufactured Ni-based superalloys

Knowledge of process-structure-property relationships to engineer better heat treatments for laser powder bed fusion additive manufactured Inconel 718

Heterogeneous structures in a Ni-based superalloy with tailoring mechanical properties produced by a twin laser powder bed fusion system

Mechanical Behavior of Laser Powder Bed Fusion Processed Inconel 625 Alloy

In Situ Alloying of a Modified Inconel 625 via Laser Powder Bed Fusion: Microstructure and Mechanical Properties

Experimental Investigations into the Effect of Infill Patterns on the Microstructure and Mechanical Properties of Inconel 718 Using Laser-Directed Energy Deposition

Microstructures and High-Temperature Mechanical Properties of Inconel 718 Superalloy Fabricated via Laser Powder Bed Fusion