Abstract:A simple process to synthesize metal nitride particles was proposed using submerged arc discharge plasma in liquid nitrogen. Gibbs standard free energy was considered for the selection of the nitride-forming materials. In this study, titanium (Ti) and aluminum (Al) electrodes were used as raw materials for nitride particle preparation. Liquid nitrogen acted as a dielectric medium as well as a nitridation source in this process. A copper electrode was also used as a non-reactive material for comparison with the reactive Ti and Al electrodes. As the operating conditions of the experiments, the arc discharge current was varied from 5 A (low-power mode) to 30 A (high-power mode). The formation of titanium nitride (TiN) and aluminum nitride (AlN) was confirmed in the particles prepared in all experimental conditions by X-ray powder diffraction (XRD). The observation using a field emission scanning electron microscope (FE-SEM) and a field emission transmission electron microscope (FE-TEM) indicated that the synthesized TiN particles showed a cubic morphology, whereas AlN particles containing unreacted Al showed a spherical morphology. The experiments using different metal electrode configurations showed that the anode generated most of the particles in this process. Based on the obtained results, a particle formation mechanism was proposed.

Direct Synthesis of AlN Nano Powder by Dielectric Barrier Discharge Plasma Assisted High-Energy Ball Milling

Synthesis of Aluminum Nitride Powders from A Plasma-Assisted Ball Milled Precursor Through Carbothermal Reaction

Synthesis of Nano-Size AlN Powders by Carbothermal Reduction from Plasma-Assisted Ball Milling Precursor

In Situ Synthesis of AlN Nanoparticles by Solid State Reaction from Plasma Assisted Ball Milling Al and Diaminomaleonitrile Mixture

Comparative Research of Plasma-Assisted Milling and Traditional Milling in Synthesizing AlN

Synthesis of AlN from Al2O3activated by plasma assisted ball milling

Effect of Different Precursors on Synthesized AlN by Plasma-Assisted Ball Milling

Synthesizing AlN powder by mechanochemical reaction between aluminum and melamine

Synergism of Mechanical Milling and Dielectric Barrier Discharge Plasma on the Fabrication of Nano-Powders of Pure Metals and Tungsten Carbide

Facile synthesis of monodisperse aluminum nitride microspheres

High purity and good dispersity AlN nanoparticles synthesized by an arc discharge with assistance of direct nitridation

Novel Way to Synthesize Nanocrystalline Aluminum Nitride from Coarse Aluminum Powder

Mechanical activation assisted combustion synthesis of AlN-Al2O3 composite ceramic powder

Evolution of Metal Nitriding and Hydriding Reactions During Ammonia Plasma-Assisted Ball Milling

Synthesis of Aluminum Nitride Using Sodium Aluminate as Aluminum Source

Aluminum nanoparticles manufactured using a ball-milling method with ammonium chloride as a grinding aid: achieving energy release at low temperature

Preparation of Metal Nitride Particles Using Arc Discharge in Liquid Nitrogen

Synthesis of NiAl(Cr,Nb) Powder by Mechanical Alloying

Fabrication Of Nanostructural Aluminum Alloy Powder With Ball Milling Method

Effect of solvent and processing condition on structure and morphology of aluminum nitride nanopowders fabricated by electrical explosion of wire (EEW)

SYNTHESIS OF ALUMINUM NITRIDE POWDER BY IN SITU REACTION