Abstract:The A15 phase superconductor Nb3Al has been considered as an alternative to Nb3Sn for high field and large scale applications. However, to prepare a stoichiometric Nb3Al with fine grain structures is very difficult. High-energy ball milling is a solid state powder processing technique and is a very useful for preparing Nb-Al alloys (Nb3Al). The effects of ball milling time and annealing temperature on the formation of Nb3Al superconducting phase have been studied. Pure Nb and Al powders with stoichiometric ratio of Nb3Al were mixed and milled, and the charging and milling were performed in an inert atmosphere. Phase formation and structural evolution during high-energy ball milling have been examined by X-ray diffraction. Al disappeared and Nb peaks broadened after about one hour of milling. With increasing milling time, the peaks of Nb became considerably broader and intensities decreased, the Nb-Al solid solution phase was extensive when milled about 3 hours. In order to obtain Nb3Al superconducting phase, a subsequent anneal was required. We have annealed the as-milled powders at 800-900°C for different times to prepared Nb3Al superconducting alloy. The results indicated that Nb3Al with small amount of impurity phase can be obtained on annealing the Nb-Al solid solution phase and the superconducting transition temperature was about 15K, but it is difficult to obtain a homogeneous Nb3Al phase by annealing the amorphous powder.

Effect of Different Precursors on Synthesized AlN by Plasma-Assisted Ball Milling

Synthesis of Nano-Size AlN Powders by Carbothermal Reduction from Plasma-Assisted Ball Milling Precursor

Comparative Research of Plasma-Assisted Milling and Traditional Milling in Synthesizing AlN

Synthesis of AlN from Al2O3activated by plasma assisted ball milling

In Situ Synthesis of AlN Nanoparticles by Solid State Reaction from Plasma Assisted Ball Milling Al and Diaminomaleonitrile Mixture

Synthesis of Aluminum Nitride Powders from A Plasma-Assisted Ball Milled Precursor Through Carbothermal Reaction

Direct Synthesis of AlN Nano Powder by Dielectric Barrier Discharge Plasma Assisted High-Energy Ball Milling

Preparation of Nb3al by High-Energy Ball Milling and Superconductivity

Mechanical activation assisted combustion synthesis of AlN-Al2O3 composite ceramic powder

Synthesizing AlN powder by mechanochemical reaction between aluminum and melamine

Synthesized by Ball Milling Al-Pb-Si-Sn-Cu Nanocrystalline Powder

On Advancemeat of Carbothermal Reduction of Alumina by High Energy Ball Milling

Study on the nano-crystalline and amorphous Al-Pb series powders synthesized by mechanical alloying

Facile synthesis of monodisperse aluminum nitride microspheres

Evolution of Metal Nitriding and Hydriding Reactions During Ammonia Plasma-Assisted Ball Milling

Preparation of α-Al2O3 by low-temperature calcining γ-Al2O3 with α-phase seed in-situ obtained by ball milling

Aluminum nanoparticles manufactured using a ball-milling method with ammonium chloride as a grinding aid: achieving energy release at low temperature

Fabrication Of Nanostructural Aluminum Alloy Powder With Ball Milling Method

Characterization of MCrAlY/nano-Al2O3 nanocomposite powder produced by high-energy mechanical milling as feedstock for high-velocity oxygen fuel spraying deposition

Preparation of Aln Films by Pulsed Laser Deposition Using Sintered Aluminum Nitride and Elemental Aluminum As Raw Materials

Synthesis of AlN nanocrystalline powders