Zirconium diboride powders synthesized by boro/carbothermal reaction using sol-gel technology

Huiming Ji,Hongna Fan,Hongjun Feng,Xiaohong Sun
DOI: https://doi.org/10.1007/s12209-015-2474-0
2015-01-01
Transactions of Tianjin University
Abstract:A single phase of zirconium diboride(ZrB 2 )powder was successfully synthesized by sol-gel method in Zr-B-C-O system, using zirconium oxychloride(ZrOCl 2 ·8H 2 O), nano-scale boron and sucrose(C 12 H 22 O 11 )as the starting materials and propylene oxide(PO)as complexing agent at a low temperature. Simultaneously, the experimental and theoretical studies of ZrB 2 synthesized by boro/carbothermal reduction from novel sol-gel technology were discussed. The results indicated that the pure rod-like ZrB2 powder without residual ZrO 2 phase could be obtained with a B/Zr molar ratio of 3.5 at 1 400°C in argon atmosphere. Besides, in this study, a kinetic model for the Zr-B-C-O system producing ZrB 2 by boro/carbothermal reaction was established based on thermodynamic analysis. It was also observed that, with the increase of reaction temperature, the reaction which produced ZrB 2 powders changed from the borothermal reaction to boro/carbothermal reaction in the Zr-B-C-O system.
What problem does this paper attempt to address?