Abstract:The deposition of nanoscaled structures with a desired shape on the intended position of the substrate material is crucial for nanomaterial applications. Electron beam-induced deposition with a highly focused beam enables achievement of high accuracy and precision in this respect. Hence, we investigated the focused-electron-beam-induced deposition of Ru-containing deposits on SiO2 and sputter-cleaned silicon in ultrahigh vacuum to achieve comparably clean and morphologically well-defined Ru nanomaterials, which is relevant especially in the field of mask repair for extreme ultraviolet lithography. The precursor Ru(CO)4I2 was held at 340–345 K, and the applied electron doses were varied from 1.56 to 9.36 C/cm2 using a focused electron beam (5 keV, 1.5 nA, and 10 nm diameter). Local Auger electron spectroscopy along with subsequent sophisticated fitting procedures not only revealed the elemental composition but also enabled determination of the thickness of the fabricated deposits. Ru contents of up to 56% can be achieved at lower electron doses; at higher doses, the Ru content decreases to 45% and simultaneously the content increases. The initially lower I content is attributed to simultaneous focused electron beam-induced etching, which is found to be competing with the deposition process. The etching is evidenced by atomic force microscopy, where the structures are observed to have negative apparent height for low electron doses. With increasing electron doses, the deposits exhibit positive apparent heights because the etching is less pronounced at higher electron doses, once the Ru surface coverage has increased. The high Ru content and difficult balance between electron-induced deposition and etching considerably expand the possibilities of engineering nanostructured materials.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acsanm.1c04481.AES on a Ru crystal before and after sputtering (Figure S1), AES on a clean Ru crystal with E × N(E) versus E and dN/dE versus E signal types (Figure S2), AES on clean Ag and Ru substrates with E × N(E) versus E and dN/dE versus E signal types (Figure S3), AES on the SiO2 substrate before and after sputtering (Figure S4), AES intensities of the SiMNN peak (1615 eV) under different electron doses (Figure S5), AES damping SiMNN signal for clean Si and 5 and 3 keV FEBID structures (Figure S6), calculations for the precursor flux and current density (Section S1), and calculations for the attenuation length, thickness estimation, and information depth (Section S2) (PDF)This article has not yet been cited by other publications.

Selectivity and Growth Rate Modulations for Ruthenium Area‐selective Deposition by Co‐Reagent and Nanopattern Design

Area Selective Deposition of Ru on W/SiO2 Nanopatterns Via Sequential Reactant Dosing and Thermal Defect Correction

Direct Fabrication of Bi-Metallic PdRu Nanorod Assemblies for Electrochemical Ammonia Synthesis

Photocatalytic Surface Initiation for Area-Selective Chemical Vapor Deposition of Polymer Thin Film

Area-selective atomic layer deposition of Ru thin films by chemo-selective inhibition of alkyl aldehyde molecules on nitride surfaces

Increased selectivity in area-selective ALD by combining nucleation enhancement and SAM-based inhibition

(Invited) Area-Selective Atomic Layer Deposition of Manganese Oxides on Metal−Dielectric Patterns

Effects of Dissolved Nitrogen in Improving Barrier Properties of Ruthenium

“Dual-Tone” Area-Selective Deposition: Selectivity Inversion of Polymer on Patterned Si/SiO 2 Starting Surfaces

Smooth, Low-Resistance, Pinhole-Free, Conformal Ruthenium Films by Pulsed Chemical Vapor Deposition

Selective Atomic Layer Deposition to Extend Moore’s Law and Beyond: Surface Kinetic Tuning for Self-Aligned Growth

Inherently Selective Atomic Layer Deposition and Applications

Area selective CVD of metallic films from molybdenum, iron, and ruthenium carbonyl precursors: Use of ammonia to inhibit nucleation on oxide surfaces

Area Selective Deposition for Bottom-up Atomic-Scale Manufacturing

Inherently Area-Selective Atomic Layer Deposition of Manganese Oxide through Electronegativity-Induced Adsorption

Area-Selective Atomic Layer Deposition of Metal Oxides on Noble Metals through Catalytic Oxygen Activation

Effect of Al Precursor’s Properties on Interactions with Self-Assembled Monolayers for Area Selective Deposition

Nucleation of Co and Ru Precursors on Silicon with Different Surface Terminations: Impact on Nucleation Delay.

Chemistry for Positive Pattern Transfer Using Area-Selective Atomic Layer Deposition

Nanoscale Ruthenium-Containing Deposits from Ru(CO) 4 I 2 via Simultaneous Focused Electron Beam-Induced Deposition and Etching in Ultrahigh Vacuum: Mask Repair in Extreme Ultraviolet Lithography and Beyond

Improving Area-Selective Molecular Layer Deposition by Selective SAM Removal