Abstract:Area-selective atomic layer deposition (AS-ALD) is a highly sought-after strategy for the fabrication of next-generation electronics. This work reveals how key precursor design parameters strongly influence the efficacy of AS-ALD by comparing a series of precursors possessing the same metal center but different ligands. When the number of methyl and chloride groups in Al(CH3)xCl3–x (x = 0, 2, and 3) and the chain length of alkyl ligands in AlCyH2y+1 (y = 1 and 2) are changed, the effect of precursor chemistry (reactivity and molecular size) on the selectivity is elucidated. The results show that optimized parameters for the Al2O3 ALD processes on a self-assembled monolayer (SAM)-terminated substrate, which serves as the nongrowth surface, differ significantly from those on a Si substrate. Chlorine-containing precursors need a much longer purging time on the SAMs because of a stronger Lewis acidity compared to that of alkyl precursors. With reoptimized conditions, the ALD of Al2O3 using the Al(C2H5)3 precursor is blocked most effectively by SAM inhibitors, whereas the widely employed Al(CH3)3 precursor is blocked least effectively among the precursors tested. Finally, we show that a selectivity exceeding 0.98 is achieved for up to 75 ALD cycles with Al(C2H5)3, for which 6 nm of Al2O3 film grows selectively on SiO2-covered Si. Quantum chemical calculations show significant differences in the energetics of dimer formation across the Al precursors, with only ∼1% of AlCl3 and Al(CH3)2Cl precursors but 99% of the alkyl precursors, Al(CH3)3 and Al(C2H5)3, existing as monomers at 200 °C. We propose that a combination of precursor reactivity and effective molecular size affects the blocking of the different precursors, explaining why Al(C2H5)3, with weaker Lewis acidity and relatively large size, exhibits the best blocking results.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acs.chemmater.0c04718?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acs.chemmater.0c04718</a>.WCA with increasing ALD cycle number (Figure S1); growth per cycle of Al2O3 on Si as a function of precursor purging time (Figure S2); amount of Al/(Al + Si) and Al/(Al + Au) for AlCl3 and Al(CH3)3 on ODTS/Si and ODT/Au (Figure S3) (<a class="ext-link" href="/doi/suppl/10.1021/acs.chemmater.0c04718/suppl_file/cm0c04718_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

Effect of Al Precursor’s Properties on Interactions with Self-Assembled Monolayers for Area Selective Deposition

Role of Precursor Choice on Area-Selective Atomic Layer Deposition

Photocatalytic Surface Initiation for Area-Selective Chemical Vapor Deposition of Polymer Thin Film

Relation between Reactive Surface Sites and Precursor Choice for Area-Selective Atomic Layer Deposition Using Small Molecule Inhibitors

Sequential Use of Orthogonal Self‐Assembled Monolayers for Area‐Selective Atomic Layer Deposition of Dielectric on Metal

Unravelling the Selective Growth Mechanism of AlOx with Dimethylaluminum Isopropoxide As a Precursor in Atomic Layer Deposition: a Combined Theoretical and Experimental Study

Design and Self-catalytic Mechanism of Aluminum Precursors Bearing Amino Ligands for Al2S3 Atomic Layer Deposition

Area-Selective Atomic Layer Deposition Using Si Precursors as Inhibitors

Selective Atomic Layer Deposition to Extend Moore’s Law and Beyond: Surface Kinetic Tuning for Self-Aligned Growth

Area-Selective Atomic Layer Deposition of TiN Using Trimethoxy(octadecyl)silane as a Passivation Layer

Molecular Mechanism of Selective Al2O3 Atomic Layer Deposition on Self-Assembled Monolayers

Organosulfide Inhibitor Instigated Passivation of Multiple Substrates for Area-Selective Atomic Layer Deposition of HfO 2

Inherently Selective Atomic Layer Deposition and Applications

Area selective atomic layer deposition of titanium dioxide: Effect of precursor chemistry

Inherently Area-Selective Atomic Layer Deposition of Manganese Oxide through Electronegativity-Induced Adsorption

Area-Selective ALD with Soft Lithographic Methods: Using Self-Assembled Monolayers to Direct Film Deposition

Area-Selective Atomic Layer Deposition Using Self-Assembled Monolayer and Scanning Probe Lithography

Surface Reaction Kinetics for Inherent Selective Atomic Layer Deposition of Tantalum Oxide

Spatial Control over Atomic Layer Deposition Using Microcontact-Printed Resists

Blocking mechanisms in area-selective ALD by small molecule inhibitors of different sizes: Steric shielding versus chemical passivation

Area Selective Deposition for Bottom-up Atomic-Scale Manufacturing