Abstract:We describe here a simple and low-cost method to prepare ultra-thin, homogeneous, and transferable films of pristine carbon nanotubes (CNTs). The highly efficient chemical vapor deposition (CVD) growth method involves silica supported catalysts and alcohol vapor as gaseous carbon source. By varying the amount of catalysts, the thickness of synthesized films can be easily tuned from 20 nm (sub-monolayer) to 150 nm in a controlled fashion. High-resolution transmission electron microscopy (HRTEM) revealed that the films are composed primarily of single-walled and a small fraction of double-walled CNTs. A nonlinear relationship between film conductivity and thickness was observed. Our sub-monolayer (similar to 20 nm) film, which is noticeably thinner than conductive CNT films synthesized using other methods (typically > 50 nm and up to similar to 100 mu m), shows the highest conductivity of 400 mho . cm(-1) with similar to 90% transparency in the visible range and close to 100% transparency in the infrared range. This ultra-thin film can also be transferred carrier-film free to a wide range of substrates including low-cost plastics for flexible electronics. Compared to CNT films prepared by filtration techniques, our films demonstrated superior stability against mechanical bending.

Facile synthesis of carbon nanotubes via low temperature pyrolysis of ferrocene

A one-step single source route to carbon nanotubes

Influence of Mesoporous Materials on the Preparation of Carbon Nanotubes

Transferable thin films of pristine carbon nanotubes.

Preparation of Carbon Nanotubes at the Surface of Fe/SBA-15 Mesoporous Molecular Sieve

Production of novel amorphous carbon nanostructures from ferrocene in low-temperature solution

Synthesis of Thin-walled Carbon Nanotubes

Large-Scale and Selective Synthesis of Carbon Nanofiber Bundles, Curved Carbon Nanofibers and Helical Carbon Nanofibers.

Synthesis and Characterizations of Amorphous Carbon Nanotubes by Pyrolysis of Ferrocene Confined Within Aam Templates

Effects of Temperature and Catalyst Concentration on the Growth of Aligned Carbon Nanotubes

Large‐Scale Synthesis, Annealing, Purification, and Magnetic Properties of Crystalline Helical Carbon Nanotubes with Symmetrical Structures

Single Walled 0.4 Nm Carbon Nanotube Bundles Prepared By Pyrolysis Of N-Hexane Catalyzed By Ferrocene

Aligned Cnx Nanotubes By Pyrolysis Of Ferrocene/C-60 Under Nh3 Atmosphere

Pyrolytic Synthesis of Conical Carbon Fibers with Carbon Nanotube Tips on Carbon Substrates

Synthesis and Characterization of Fe/C Core–shell Nanoparticles

Formation of coal-based carbon nanotubes by Fe-K catalyst

Synthesis of carbon nanotubes filled with Fe3C nanowires by CVD with titanate modified palygorskite as catalyst

A New Method for Synthesizing Double-Walled Carbon Nanotubes

Preparation of Fe-Filled Carbon Nanotubes by Catalytic Decomposition of Cyclohexane

Characterization and Magnetic Properties of Helical Carbon Nanotubes and Carbon Nanobelts Synthesized in Acetylene Decomposition over Fe−Cu Nanoparticles at 450 °C

Preparation of High Purity Carbon Nano -Tubes from Ethylene Decomposition over Nanosized Iron- Based Catalysts