Abstract:Fe-filled carbon nanotubes were considered as excellent microwave adsorption materials [1], biomedicine materials [2] and high density magnetic recoding media [3]. The films produced in previous reports mainly range from a few nanometers to several microns. Here, a new method is reported for one-step synthesizing macroscopic Fe-filled CNTs film with a relatively high area. The experiment was carried out in a quartz tubular furnace by catalytic decomposing of ferrocene/dichlorobenzene. The method used is similar to that reported in Ref. [4], however some improvements were made. In the experiments additional substrates were not needed for Fe-filled CNTs growth. The Fe-filled CNTs directly grow on the interior wall of the quartz tube. The procedure is described as follows: the ferrocene was dissolved in dichlorobenzene to form a solution of 0.06 g/ml, which was then pumped continuously into a two-zone tubular quartz reactor by a flux pump at a feeding rate of 0.13 ml/min. The flowing rates of Ar/H2 during the reaction were kept at 2000/ 300 ml/min. The temperatures at preheating zone and decomposition zone were maintained at 250 and 860 , respectively. Finally, the furnace was cooled down to ambient temperature in an Ar flow. The films were easily peeled off from the interior wall of the quartz tube. Fig. 1(a) is a TEM image of Fe-filled CNTs film. The diameter of CNTs is homogeneous and foreign impurities or particles were seldom. The area of the film is about 100 cm. Most CNTs are filled with continuous and straight Fe nanowires. The Fe nanowires are about 1~3 m in length and 20~30 nm in diameter. The diameter of CNTs varies from 20 to 40 nm. XRD results show that the filled Fe nanowires are -Fe and -Fe. Annealing process was used to transformed the -Fe into -Fe. The Fe-filled CNTs films were annealed at 650 for 15 h in Ar atmosphere. As show in Fig. 1(b), almost all of filled Fe nanowires were -Fe after annealing.

Preparation of Fe-Filled Carbon Nanotubes by Catalytic Decomposition of Cyclohexane

Preparation of Carbon Nanotubes at the Surface of Fe/SBA-15 Mesoporous Molecular Sieve

Influence of Mesoporous Materials on the Preparation of Carbon Nanotubes

Direct Synthesis of Fe-Filled Carbon Nanotubes Macro-Film by Catalytic Decomposition Method

Synthesis of carbon nanotubes filled with Fe3C nanowires by CVD with titanate modified palygorskite as catalyst

Preparation of High Purity Carbon Nano -Tubes from Ethylene Decomposition over Nanosized Iron- Based Catalysts

Preparation and Purification of Carbon Nanotubes by Catalytic Decomposition

Synthesis and Growth Mechanism of Fe-Catalyzed Carbon Nanotubes by Plasma-Enhanced Chemical Vapor Deposition

Preparation of Carbon Nanotubes and Their Application in the Direct Oxidation of Cyclohexene Catalyzed by Ru Complex

3d Transition Metals and Oxides within Carbon Nanotubes by Co-Pyrolysis of Metallocene & Camphor: High Filling Efficiency and Self-Organized Structures

The Decisive Roles of Chlorine-Contained Precursor and Hydrogen for the Filling Fe Nanowires into Carbon Nanotubes

Preparation of Fe–Ni Alloy Nanoparticles Inside Carbon Nanotubes Via Wet Chemistry

Fe2O3 Particles Encapsulated Inside Aligned CNx Nanotubes

In Situ TEM Observation of the Gasification and Growth of Carbon Nanotubes Using Iron Catalysts

Growth of Carbon Nanotubes with Metal-Loading Mesoporous Molecular Sieves Catalysts

Characterization and Magnetic Properties of Helical Carbon Nanotubes and Carbon Nanobelts Synthesized in Acetylene Decomposition over Fe−Cu Nanoparticles at 450 °C

Formation Mechanism of Carbon Encapsulated Fe Nanoparticles in the Growth of Single-/Double-walled Carbon Nanotubes

Catalysts effect on morphology of carbon nanotubes prepared by catalytic chemical vapor deposition in a nano-agglomerate bed

Pre-heating effect on the catalytic growth of partially filled carbon nanotubes by chemical vapor deposition

Carburization of Fe/Ni Catalyst for Efficient Growth of Single-Walled Carbon Nanotubes

Catalytic Decomposition of CH4 to Hydrogen and Carbon Nanotubes Using the Pt(1)-Fe(30)/MCM-41 Catalyst