Abstract:Fe-filled carbon nanotubes were considered as excellent microwave adsorption materials [1], biomedicine materials [2] and high density magnetic recoding media [3]. The films produced in previous reports mainly range from a few nanometers to several microns. Here, a new method is reported for one-step synthesizing macroscopic Fe-filled CNTs film with a relatively high area. The experiment was carried out in a quartz tubular furnace by catalytic decomposing of ferrocene/dichlorobenzene. The method used is similar to that reported in Ref. [4], however some improvements were made. In the experiments additional substrates were not needed for Fe-filled CNTs growth. The Fe-filled CNTs directly grow on the interior wall of the quartz tube. The procedure is described as follows: the ferrocene was dissolved in dichlorobenzene to form a solution of 0.06 g/ml, which was then pumped continuously into a two-zone tubular quartz reactor by a flux pump at a feeding rate of 0.13 ml/min. The flowing rates of Ar/H2 during the reaction were kept at 2000/ 300 ml/min. The temperatures at preheating zone and decomposition zone were maintained at 250 and 860 , respectively. Finally, the furnace was cooled down to ambient temperature in an Ar flow. The films were easily peeled off from the interior wall of the quartz tube. Fig. 1(a) is a TEM image of Fe-filled CNTs film. The diameter of CNTs is homogeneous and foreign impurities or particles were seldom. The area of the film is about 100 cm. Most CNTs are filled with continuous and straight Fe nanowires. The Fe nanowires are about 1~3 m in length and 20~30 nm in diameter. The diameter of CNTs varies from 20 to 40 nm. XRD results show that the filled Fe nanowires are -Fe and -Fe. Annealing process was used to transformed the -Fe into -Fe. The Fe-filled CNTs films were annealed at 650 for 15 h in Ar atmosphere. As show in Fig. 1(b), almost all of filled Fe nanowires were -Fe after annealing.

The Decisive Roles of Chlorine-Contained Precursor and Hydrogen for the Filling Fe Nanowires into Carbon Nanotubes

Effect of Using Chlorine-Containing Precursors in the Synthesis of FeNi-filled Carbon Nanotubes

Water-Assisted Preparation of High-Purity Semiconducting (14,4) Carbon Nanotubes

One-dimensional Sub-stoichiometric W3O8Nanowires Filled Carbon Nanotubes

Long Continuous FeNi Nanowires Inside Carbon Nanotubes: Synthesis, Property and Application

In-situ filling of Fe/Ni oxide nanowire into carbon nanotubes doped with nitrogen in CH4/H2/air plasmas

<i>In Situ</i> Filling of Fe/Ni Oxide Nanowire into Carbon Nanotubes Doped with Nitrogen in CH<sub>4</sub>/H<sub>2</sub>/Air Plasma

Synthesis, Field Emission and Microwave Absorption of Carbon Nanotubes Filled with Ferromagnetic Nanowires

Preparation of Fe-Filled Carbon Nanotubes by Catalytic Decomposition of Cyclohexane

Enhanced Field Emission of Open-Ended, Thin-Walled Carbon Nanotubes Filled with Ferromagnetic Nanowires

Direct Synthesis of Fe-Filled Carbon Nanotubes Macro-Film by Catalytic Decomposition Method

Filling Double-Walled Carbon Nanotubes with WO3 and W Nanowires Via Confined Chemical Reactions.

The influence of ethanol on the growth and structure of carbon nanotubes

Carbon Nanofiber Microspheres Obtained from Ethylene Using Fecl3 As the Catalyst Precursor

Filling of single-walled carbon nanotubes with silver

The Large-Scale Synthesis and Characterization of Carbon Nanotubes Filled with Long Continuous Inorganic Nanowires in Supercritical CS2

Quantum chemical simulations reveal acetylene-based growth mechanisms in the chemical vapor deposition synthesis of carbon nanotubes

FEW WALLED CARBON NANOTUBE PRODUCTION IN LARGE-SCALE BY NANO-AGGLOMERATE FLUIDIZED-BED PROCESS

Progress in Preparation of Metal-filled Carbon Nanotubes

Formation Mechanism of Carbon Encapsulated Fe Nanoparticles in the Growth of Single-/Double-walled Carbon Nanotubes

Preparation, Electromagnetic and Enhanced Microwave Absorption Properties of Fe Nanoparticles Encapsulated in Carbon Nanotubes