Abstract:Fe-filled carbon nanotubes were considered as excellent microwave adsorption materials [1], biomedicine materials [2] and high density magnetic recoding media [3]. The films produced in previous reports mainly range from a few nanometers to several microns. Here, a new method is reported for one-step synthesizing macroscopic Fe-filled CNTs film with a relatively high area. The experiment was carried out in a quartz tubular furnace by catalytic decomposing of ferrocene/dichlorobenzene. The method used is similar to that reported in Ref. [4], however some improvements were made. In the experiments additional substrates were not needed for Fe-filled CNTs growth. The Fe-filled CNTs directly grow on the interior wall of the quartz tube. The procedure is described as follows: the ferrocene was dissolved in dichlorobenzene to form a solution of 0.06 g/ml, which was then pumped continuously into a two-zone tubular quartz reactor by a flux pump at a feeding rate of 0.13 ml/min. The flowing rates of Ar/H2 during the reaction were kept at 2000/ 300 ml/min. The temperatures at preheating zone and decomposition zone were maintained at 250 and 860 , respectively. Finally, the furnace was cooled down to ambient temperature in an Ar flow. The films were easily peeled off from the interior wall of the quartz tube. Fig. 1(a) is a TEM image of Fe-filled CNTs film. The diameter of CNTs is homogeneous and foreign impurities or particles were seldom. The area of the film is about 100 cm. Most CNTs are filled with continuous and straight Fe nanowires. The Fe nanowires are about 1~3 m in length and 20~30 nm in diameter. The diameter of CNTs varies from 20 to 40 nm. XRD results show that the filled Fe nanowires are -Fe and -Fe. Annealing process was used to transformed the -Fe into -Fe. The Fe-filled CNTs films were annealed at 650 for 15 h in Ar atmosphere. As show in Fig. 1(b), almost all of filled Fe nanowires were -Fe after annealing.

Long Continuous FeNi Nanowires Inside Carbon Nanotubes: Synthesis, Property and Application

Enhanced Field Emission of Open-Ended, Thin-Walled Carbon Nanotubes Filled with Ferromagnetic Nanowires

Effect of Using Chlorine-Containing Precursors in the Synthesis of FeNi-filled Carbon Nanotubes

One-dimensional Sub-stoichiometric W3O8Nanowires Filled Carbon Nanotubes

Super-long continuous Ni nanowires encapsulated in carbon nanotubes.

Synthesis, Field Emission and Microwave Absorption of Carbon Nanotubes Filled with Ferromagnetic Nanowires

The Large-Scale Synthesis and Characterization of Carbon Nanotubes Filled with Long Continuous Inorganic Nanowires in Supercritical CS2

Super-long continuous Ni nanowires encapsulated in carbon nanotubesElectronic supplementary information (ESI) available: SEM images. See http://www.rsc.org/suppdata/cc/b4/b405444j/

Growth and Nanoscale Magnetic Properties of Ferromagnetic Nanowire Encapsulated Inside Carbon Nanotubes

Preparation of Fe–Ni Alloy Nanoparticles Inside Carbon Nanotubes Via Wet Chemistry

Direct Synthesis of Fe-Filled Carbon Nanotubes Macro-Film by Catalytic Decomposition Method

The Decisive Roles of Chlorine-Contained Precursor and Hydrogen for the Filling Fe Nanowires into Carbon Nanotubes

Preparation, Electromagnetic and Enhanced Microwave Absorption Properties of Fe Nanoparticles Encapsulated in Carbon Nanotubes

Continuous preparation of carbon nanotube fiber and its potential applications in electrical, thermal, mechanical and biosensing fields

A Novel Continuous Carbon Nanotube Fiber/carbon Composite by Electrified Preform Heating Chemical Vapor Infiltration

Microwave Absorbing Properties Of Fe-Filled Carbon Nanotubes/Epoxy Composite In 2-18ghz

Improved Filling Rate and Enhanced Magnetic Properties of Fe-filled Carbon Nanotubes by Annealing and Magnetic Separation

Template synthesis, characterization and magnetic property of Fe nanowires-filled amorphous carbon nanotubes array

Filling Double-Walled Carbon Nanotubes with WO3 and W Nanowires Via Confined Chemical Reactions.

3d Transition Metals and Oxides within Carbon Nanotubes by Co-Pyrolysis of Metallocene & Camphor: High Filling Efficiency and Self-Organized Structures

Carbon Nanotubes Filled with Ferromagnetic Alloy Nanowires: Lightweight and Wide-Band Microwave Absorber