Abstract:In this study, C/C–SiC and C/C–SiC–ZrC composites were prepared via chemical vapor infiltration and polymer infiltration pyrolysis, and the ablation mechanism under hypersonic oxygen-rich environmental conditions was investigated. The C/C–SiC composites demonstrate an excellent ablation resistance in a hypersonic oxygen-rich environment with a relatively low temperature and speed of approximately 1800 K and 1100 m/s, respectively. It is only in the ablation center area with higher temperatures that a certain degree of thermochemical ablation was observed. The mass and linear ablation rates of C/C–SiC composites (0.027 g/s and 0.117 mm/s, respectively) showed a significant increase in a hypersonic oxygen-rich environment with a temperature and velocity of approximately 2050 K and 2000 m/s, respectively. The high-temperature ablation resistance of ZrC-modified C/C–SiC–ZrC composites improved significantly. However, the ZrC ceramic component had a considerable impact on the ablation resistance of the material. The structural integrity of C/C–20SiC–30ZrC composites was relatively high in hypersonic oxygen-rich environments with a jet temperature and velocity of 2050 K and 2000 m/s, respectively, and mass and linear ablation rates were 0.012 g/s and 0.015 mm/s, respectively. When the ZrC content increased by 40%, the ablation resistance of the composite reduced significantly, whereas the mass and linear ablation rates increased to 0.043 g/s and 0.130 mm/s, respectively.

Ablation Properties of C/C-ZrC-SiC Composites

Ablation Properties of C/C-Zrc-Sic Composites by the Precursor Infiltration Pyrolysis

Mechanical Properties and Ablation Behavior of C/C-ZrC and C/C-ZrC-SiC Composites Prepared by Precursor Infiltration and Pyrolysis Combined with Chemical Vapor Infiltration

Ablation Behavior of ZrC–SiC Coated C/C–ZrC–SiC Composites Prepared by Precursor Infiltration Pyrolysis Combined with Reactive Melt Infiltration

Effects of Porous C/C Density on the Densification Behavior and Ablation Property of C/C–ZrC–SiC Composites

Preparation, Ablation Behavior and Mechanism of C/C-ZrC-SiC and C/C-SiC Composites

Ablation Behavior of a C/C-ZrC-SiC Composite Based on High-Solid-loading Slurry Impregnation under Oxyacetylene Torch

Effect of C/C density on the properties of C/C-SiC-ZrC composites

Ablation Properties of 2D C/SiC-ZrB2 Composite

Ablative and Mechanical Properties of C/C–ZrC Composites Prepared by Precursor Infiltration and Pyrolysis Process

Effect of ZrC–SiC Content on Microstructure and Ablation Properties of C/C Composites

The Ablation Behavior and Mechanical Property of C/C-SiC-ZrB2 Composites Fabricated by Reactive Melt Infiltration

Microstructure and Ablation Behavior of SiC Coated C/C–SiC–ZrC Composites Prepared by a Hybrid Infiltration Process

Ablation mechanism of C/C–SiC and C/C–SiC–ZrC composites in hypersonic oxygen-enriched environment

Enhanced Anti-Ablation Performance of Carbon/carbon Composites Modified with ZrC-SiC

Ablation Performances of Multi-Phased C/C-Zrc-Sic Ultra-High Temperature Composites

Preparation and ablation properties of ZrC-SiC coating for carbon/carbon composites by solid phase infiltration

Fabrication and properties of 2D C/C-ZrB2-ZrC-SiC composites by hybrid precursor infiltration and pyrolysis

Ablation Behavior of C/C-ZrC-SiC Composites Prepared by Reactive Melt Infiltration under Oxyacetylene Torch at Two Heat Fluxes

Effects of Oxidizing Species on Ablation Behavior of C/C-Zrb2-Zrc-Sic Composites Prepared by Precursor Infiltration and Pyrolysis

Microstructures and Ablation Properties of C/C−SiC−ZrC Composites Prepared Using C/C Skeletons with Various Densities